ASTM A372 Grade J Steel vs. G-CoCr28 Cobalt

ASTM A372 grade J steel belongs to the iron alloys classification, while G-CoCr28 cobalt belongs to the cobalt alloys. There are 27 material properties with values for both materials. Properties with values for just one material (4, in this case) are not shown.

For each property being compared, the top bar is ASTM A372 grade J steel and the bottom bar is G-CoCr28 cobalt.

Metric UnitsUS Customary Units

Mechanical Properties

Elastic (Young's, Tensile) Modulus, GPa 190
210
Elongation at Break, % 17 to 22
6.7
Fatigue Strength, MPa 310 to 570
130
Poisson's Ratio 0.29
0.28
Shear Modulus, GPa 73
83
Tensile Strength: Ultimate (UTS), MPa 650 to 1020
560
Tensile Strength: Yield (Proof), MPa 430 to 850
260

Thermal Properties

Latent Heat of Fusion, J/g 250
320
Maximum Temperature: Mechanical, °C 420
1200
Melting Completion (Liquidus), °C 1460
1330
Melting Onset (Solidus), °C 1420
1270
Specific Heat Capacity, J/kg-K 470
470
Thermal Conductivity, W/m-K 44
8.5
Thermal Expansion, µm/m-K 13
14

Otherwise Unclassified Properties

Base Metal Price, % relative 2.4
100
Density, g/cm3 7.8
8.1
Embodied Carbon, kg CO2/kg material 1.5
6.2
Embodied Energy, MJ/kg 20
84
Embodied Water, L/kg 51
440

Common Calculations

Resilience: Ultimate (Unit Rupture Work), MJ/m3 130 to 170
31
Resilience: Unit (Modulus of Resilience), kJ/m3 500 to 1930
160
Stiffness to Weight: Axial, points 13
15
Stiffness to Weight: Bending, points 24
24
Strength to Weight: Axial, points 23 to 36
19
Strength to Weight: Bending, points 21 to 29
19
Thermal Diffusivity, mm2/s 12
2.2
Thermal Shock Resistance, points 19 to 30
14

Alloy Composition

Carbon (C), % 0.35 to 0.5
0.050 to 0.25
Chromium (Cr), % 0.8 to 1.2
27 to 30
Cobalt (Co), % 0
48 to 52
Iron (Fe), % 96.7 to 97.8
9.7 to 24.5
Manganese (Mn), % 0.75 to 1.1
0 to 1.5
Molybdenum (Mo), % 0.15 to 0.25
0 to 0.5
Nickel (Ni), % 0
0 to 4.0
Niobium (Nb), % 0
0 to 0.5
Phosphorus (P), % 0 to 0.015
0 to 0.040
Silicon (Si), % 0.15 to 0.35
0.5 to 1.5
Sulfur (S), % 0 to 0.010
0 to 0.030