ASTM A372 Grade J Steel vs. S41050 Stainless Steel

Both ASTM A372 grade J steel and S41050 stainless steel are iron alloys. They have 88% of their average alloy composition in common. There are 31 material properties with values for both materials. Properties with values for just one material (3, in this case) are not shown.

For each property being compared, the top bar is ASTM A372 grade J steel and the bottom bar is S41050 stainless steel.

Metric UnitsUS Customary Units

Mechanical Properties

Brinell Hardness 200 to 310
160
Elastic (Young's, Tensile) Modulus, GPa 190
190
Elongation at Break, % 17 to 22
25
Fatigue Strength, MPa 310 to 570
160
Poisson's Ratio 0.29
0.28
Shear Modulus, GPa 73
76
Shear Strength, MPa 410 to 630
300
Tensile Strength: Ultimate (UTS), MPa 650 to 1020
470
Tensile Strength: Yield (Proof), MPa 430 to 850
230

Thermal Properties

Latent Heat of Fusion, J/g 250
270
Maximum Temperature: Mechanical, °C 420
720
Melting Completion (Liquidus), °C 1460
1440
Melting Onset (Solidus), °C 1420
1400
Specific Heat Capacity, J/kg-K 470
480
Thermal Conductivity, W/m-K 44
27
Thermal Expansion, µm/m-K 13
10

Electrical Properties

Electrical Conductivity: Equal Volume, % IACS 7.3
2.9
Electrical Conductivity: Equal Weight (Specific), % IACS 8.4
3.3

Otherwise Unclassified Properties

Base Metal Price, % relative 2.4
7.0
Density, g/cm3 7.8
7.8
Embodied Carbon, kg CO2/kg material 1.5
1.9
Embodied Energy, MJ/kg 20
27
Embodied Water, L/kg 51
97

Common Calculations

Resilience: Ultimate (Unit Rupture Work), MJ/m3 130 to 170
98
Resilience: Unit (Modulus of Resilience), kJ/m3 500 to 1930
140
Stiffness to Weight: Axial, points 13
14
Stiffness to Weight: Bending, points 24
25
Strength to Weight: Axial, points 23 to 36
17
Strength to Weight: Bending, points 21 to 29
17
Thermal Diffusivity, mm2/s 12
7.2
Thermal Shock Resistance, points 19 to 30
17

Alloy Composition

Carbon (C), % 0.35 to 0.5
0 to 0.040
Chromium (Cr), % 0.8 to 1.2
10.5 to 12.5
Iron (Fe), % 96.7 to 97.8
84.2 to 88.9
Manganese (Mn), % 0.75 to 1.1
0 to 1.0
Molybdenum (Mo), % 0.15 to 0.25
0
Nickel (Ni), % 0
0.6 to 1.1
Nitrogen (N), % 0
0 to 0.1
Phosphorus (P), % 0 to 0.015
0 to 0.045
Silicon (Si), % 0.15 to 0.35
0 to 1.0
Sulfur (S), % 0 to 0.010
0 to 0.030