ASTM A372 Grade J Class 110 vs. ASTM A372 Grade J Class 90

Both ASTM A372 grade J class 110 and ASTM A372 grade J class 90 are variants of the same material. They share alloy composition and many physical properties, but develop different mechanical properties as a result of different processing.

For each property being compared, the top bar is ASTM A372 grade J class 110 and the bottom bar is ASTM A372 grade J class 90.

Metric UnitsUS Customary Units

Mechanical Properties

Brinell Hardness 310
280
Elastic (Young's, Tensile) Modulus, GPa 190
190
Elongation at Break, % 17
20
Fatigue Strength, MPa 570
490
Poisson's Ratio 0.29
0.29
Shear Modulus, GPa 73
73
Shear Strength, MPa 630
570
Tensile Strength: Ultimate (UTS), MPa 1020
910
Tensile Strength: Yield (Proof), MPa 850
710

Thermal Properties

Latent Heat of Fusion, J/g 250
250
Maximum Temperature: Mechanical, °C 420
420
Melting Completion (Liquidus), °C 1460
1460
Melting Onset (Solidus), °C 1420
1420
Specific Heat Capacity, J/kg-K 470
470
Thermal Conductivity, W/m-K 44
44
Thermal Expansion, µm/m-K 13
13

Electrical Properties

Electrical Conductivity: Equal Volume, % IACS 7.3
7.3
Electrical Conductivity: Equal Weight (Specific), % IACS 8.4
8.4

Otherwise Unclassified Properties

Base Metal Price, % relative 2.4
2.4
Density, g/cm3 7.8
7.8
Embodied Carbon, kg CO2/kg material 1.5
1.5
Embodied Energy, MJ/kg 20
20
Embodied Water, L/kg 51
51

Common Calculations

Resilience: Ultimate (Unit Rupture Work), MJ/m3 160
170
Resilience: Unit (Modulus of Resilience), kJ/m3 1930
1330
Stiffness to Weight: Axial, points 13
13
Stiffness to Weight: Bending, points 24
24
Strength to Weight: Axial, points 36
32
Strength to Weight: Bending, points 29
27
Thermal Diffusivity, mm2/s 12
12
Thermal Shock Resistance, points 30
27

Alloy Composition

Carbon (C), % 0.35 to 0.5
0.35 to 0.5
Chromium (Cr), % 0.8 to 1.2
0.8 to 1.2
Iron (Fe), % 96.7 to 97.8
96.7 to 97.8
Manganese (Mn), % 0.75 to 1.1
0.75 to 1.1
Molybdenum (Mo), % 0.15 to 0.25
0.15 to 0.25
Phosphorus (P), % 0 to 0.015
0 to 0.015
Silicon (Si), % 0.15 to 0.35
0.15 to 0.35
Sulfur (S), % 0 to 0.010
0 to 0.010