MakeItFrom.com
Menu (ESC)

ASTM A372 Grade L Steel vs. EN 1.0596 Steel

Both ASTM A372 grade L steel and EN 1.0596 steel are iron alloys. They have a very high 97% of their average alloy composition in common. There are 31 material properties with values for both materials. Properties with values for just one material (1, in this case) are not shown.

For each property being compared, the top bar is ASTM A372 grade L steel and the bottom bar is EN 1.0596 steel.

Metric UnitsUS Customary Units

Mechanical Properties

Brinell Hardness 350
150
Elastic (Young's, Tensile) Modulus, GPa 190
190
Elongation at Break, % 14
20
Fatigue Strength, MPa 670
230
Poisson's Ratio 0.29
0.29
Shear Modulus, GPa 73
73
Shear Strength, MPa 700
330
Tensile Strength: Ultimate (UTS), MPa 1160
530
Tensile Strength: Yield (Proof), MPa 1040
330

Thermal Properties

Latent Heat of Fusion, J/g 250
250
Maximum Temperature: Mechanical, °C 430
400
Melting Completion (Liquidus), °C 1460
1460
Melting Onset (Solidus), °C 1420
1420
Specific Heat Capacity, J/kg-K 470
470
Thermal Conductivity, W/m-K 44
50
Thermal Expansion, µm/m-K 13
12

Electrical Properties

Electrical Conductivity: Equal Volume, % IACS 7.5
7.3
Electrical Conductivity: Equal Weight (Specific), % IACS 8.6
8.3

Otherwise Unclassified Properties

Base Metal Price, % relative 3.5
1.9
Density, g/cm3 7.8
7.8
Embodied Carbon, kg CO2/kg material 1.7
1.4
Embodied Energy, MJ/kg 22
19
Embodied Water, L/kg 54
47

Common Calculations

Resilience: Ultimate (Unit Rupture Work), MJ/m3 150
93
Resilience: Unit (Modulus of Resilience), kJ/m3 2890
290
Stiffness to Weight: Axial, points 13
13
Stiffness to Weight: Bending, points 24
24
Strength to Weight: Axial, points 41
19
Strength to Weight: Bending, points 31
18
Thermal Diffusivity, mm2/s 12
14
Thermal Shock Resistance, points 34
17

Alloy Composition

Carbon (C), % 0.38 to 0.43
0 to 0.24
Chromium (Cr), % 0.7 to 0.9
0
Copper (Cu), % 0
0 to 0.6
Iron (Fe), % 95.2 to 96.3
96.8 to 100
Manganese (Mn), % 0.6 to 0.8
0 to 1.7
Molybdenum (Mo), % 0.2 to 0.3
0
Nickel (Ni), % 1.7 to 2.0
0
Phosphorus (P), % 0 to 0.015
0 to 0.035
Silicon (Si), % 0.15 to 0.35
0 to 0.6
Sulfur (S), % 0 to 0.010
0 to 0.035