ASTM A372 Grade L Steel vs. EN 1.4361 Stainless Steel

Both ASTM A372 grade L steel and EN 1.4361 stainless steel are iron alloys. They have 66% of their average alloy composition in common. There are 31 material properties with values for both materials. Properties with values for just one material (3, in this case) are not shown.

For each property being compared, the top bar is ASTM A372 grade L steel and the bottom bar is EN 1.4361 stainless steel.

Metric UnitsUS Customary Units

Mechanical Properties

Brinell Hardness 350
200
Elastic (Young's, Tensile) Modulus, GPa 190
190
Elongation at Break, % 14
43
Fatigue Strength, MPa 670
220
Poisson's Ratio 0.29
0.28
Shear Modulus, GPa 73
75
Shear Strength, MPa 700
440
Tensile Strength: Ultimate (UTS), MPa 1160
630
Tensile Strength: Yield (Proof), MPa 1040
250

Thermal Properties

Latent Heat of Fusion, J/g 250
350
Maximum Temperature: Mechanical, °C 430
940
Melting Completion (Liquidus), °C 1460
1370
Melting Onset (Solidus), °C 1420
1330
Specific Heat Capacity, J/kg-K 470
490
Thermal Conductivity, W/m-K 44
14
Thermal Expansion, µm/m-K 13
16

Electrical Properties

Electrical Conductivity: Equal Volume, % IACS 7.5
2.1
Electrical Conductivity: Equal Weight (Specific), % IACS 8.6
2.5

Otherwise Unclassified Properties

Base Metal Price, % relative 3.5
19
Density, g/cm3 7.8
7.6
Embodied Carbon, kg CO2/kg material 1.7
3.6
Embodied Energy, MJ/kg 22
52
Embodied Water, L/kg 54
150

Common Calculations

Resilience: Ultimate (Unit Rupture Work), MJ/m3 150
220
Resilience: Unit (Modulus of Resilience), kJ/m3 2890
160
Stiffness to Weight: Axial, points 13
14
Stiffness to Weight: Bending, points 24
25
Strength to Weight: Axial, points 41
23
Strength to Weight: Bending, points 31
21
Thermal Diffusivity, mm2/s 12
3.7
Thermal Shock Resistance, points 34
15

Alloy Composition

Carbon (C), % 0.38 to 0.43
0 to 0.015
Chromium (Cr), % 0.7 to 0.9
16.5 to 18.5
Iron (Fe), % 95.2 to 96.3
58.7 to 65.8
Manganese (Mn), % 0.6 to 0.8
0 to 2.0
Molybdenum (Mo), % 0.2 to 0.3
0 to 0.2
Nickel (Ni), % 1.7 to 2.0
14 to 16
Nitrogen (N), % 0
0 to 0.1
Phosphorus (P), % 0 to 0.015
0 to 0.025
Silicon (Si), % 0.15 to 0.35
3.7 to 4.5
Sulfur (S), % 0 to 0.010
0 to 0.010