ASTM A372 Grade L Steel vs. EN 1.4621 Stainless Steel

Both ASTM A372 grade L steel and EN 1.4621 stainless steel are iron alloys. They have 79% of their average alloy composition in common. There are 30 material properties with values for both materials. Properties with values for just one material (3, in this case) are not shown.

For each property being compared, the top bar is ASTM A372 grade L steel and the bottom bar is EN 1.4621 stainless steel.

Metric UnitsUS Customary Units

Mechanical Properties

Elastic (Young's, Tensile) Modulus, GPa 190
200
Elongation at Break, % 14
25
Fatigue Strength, MPa 670
190
Poisson's Ratio 0.29
0.27
Shear Modulus, GPa 73
78
Shear Strength, MPa 700
320
Tensile Strength: Ultimate (UTS), MPa 1160
500
Tensile Strength: Yield (Proof), MPa 1040
270

Thermal Properties

Latent Heat of Fusion, J/g 250
290
Maximum Temperature: Mechanical, °C 430
970
Melting Completion (Liquidus), °C 1460
1440
Melting Onset (Solidus), °C 1420
1390
Specific Heat Capacity, J/kg-K 470
480
Thermal Conductivity, W/m-K 44
21
Thermal Expansion, µm/m-K 13
11

Electrical Properties

Electrical Conductivity: Equal Volume, % IACS 7.5
2.6
Electrical Conductivity: Equal Weight (Specific), % IACS 8.6
3.1

Otherwise Unclassified Properties

Base Metal Price, % relative 3.5
14
Density, g/cm3 7.8
7.7
Embodied Carbon, kg CO2/kg material 1.7
2.8
Embodied Energy, MJ/kg 22
41
Embodied Water, L/kg 54
140

Common Calculations

Resilience: Ultimate (Unit Rupture Work), MJ/m3 150
110
Resilience: Unit (Modulus of Resilience), kJ/m3 2890
190
Stiffness to Weight: Axial, points 13
14
Stiffness to Weight: Bending, points 24
25
Strength to Weight: Axial, points 41
18
Strength to Weight: Bending, points 31
18
Thermal Diffusivity, mm2/s 12
5.7
Thermal Shock Resistance, points 34
17

Alloy Composition

Carbon (C), % 0.38 to 0.43
0 to 0.030
Chromium (Cr), % 0.7 to 0.9
20 to 21.5
Copper (Cu), % 0
0.1 to 1.0
Iron (Fe), % 95.2 to 96.3
74.4 to 79.7
Manganese (Mn), % 0.6 to 0.8
0 to 1.0
Molybdenum (Mo), % 0.2 to 0.3
0
Nickel (Ni), % 1.7 to 2.0
0
Niobium (Nb), % 0
0.2 to 1.0
Nitrogen (N), % 0
0 to 0.030
Phosphorus (P), % 0 to 0.015
0 to 0.040
Silicon (Si), % 0.15 to 0.35
0 to 1.0
Sulfur (S), % 0 to 0.010
0 to 0.015