ASTM A372 Grade L Steel vs. EN 1.4877 Stainless Steel

Both ASTM A372 grade L steel and EN 1.4877 stainless steel are iron alloys. They have 43% of their average alloy composition in common. There are 31 material properties with values for both materials. Properties with values for just one material (2, in this case) are not shown.

For each property being compared, the top bar is ASTM A372 grade L steel and the bottom bar is EN 1.4877 stainless steel.

Metric UnitsUS Customary Units

Mechanical Properties

Brinell Hardness 350
190
Elastic (Young's, Tensile) Modulus, GPa 190
200
Elongation at Break, % 14
36
Fatigue Strength, MPa 670
170
Poisson's Ratio 0.29
0.28
Shear Modulus, GPa 73
79
Shear Strength, MPa 700
420
Tensile Strength: Ultimate (UTS), MPa 1160
630
Tensile Strength: Yield (Proof), MPa 1040
200

Thermal Properties

Latent Heat of Fusion, J/g 250
310
Maximum Temperature: Mechanical, °C 430
1150
Melting Completion (Liquidus), °C 1460
1400
Melting Onset (Solidus), °C 1420
1360
Specific Heat Capacity, J/kg-K 470
470
Thermal Conductivity, W/m-K 44
12
Thermal Expansion, µm/m-K 13
15

Electrical Properties

Electrical Conductivity: Equal Volume, % IACS 7.5
1.8
Electrical Conductivity: Equal Weight (Specific), % IACS 8.6
2.0

Otherwise Unclassified Properties

Base Metal Price, % relative 3.5
37
Density, g/cm3 7.8
8.0
Embodied Carbon, kg CO2/kg material 1.7
6.2
Embodied Energy, MJ/kg 22
89
Embodied Water, L/kg 54
220

Common Calculations

Resilience: Ultimate (Unit Rupture Work), MJ/m3 150
180
Resilience: Unit (Modulus of Resilience), kJ/m3 2890
100
Stiffness to Weight: Axial, points 13
14
Stiffness to Weight: Bending, points 24
24
Strength to Weight: Axial, points 41
22
Strength to Weight: Bending, points 31
20
Thermal Diffusivity, mm2/s 12
3.2
Thermal Shock Resistance, points 34
15

Alloy Composition

Aluminum (Al), % 0
0 to 0.025
Carbon (C), % 0.38 to 0.43
0.040 to 0.080
Cerium (Ce), % 0
0.050 to 0.1
Chromium (Cr), % 0.7 to 0.9
26 to 28
Iron (Fe), % 95.2 to 96.3
36.4 to 42.3
Manganese (Mn), % 0.6 to 0.8
0 to 1.0
Molybdenum (Mo), % 0.2 to 0.3
0
Nickel (Ni), % 1.7 to 2.0
31 to 33
Niobium (Nb), % 0
0.6 to 1.0
Nitrogen (N), % 0
0 to 0.1
Phosphorus (P), % 0 to 0.015
0 to 0.020
Silicon (Si), % 0.15 to 0.35
0 to 0.3
Sulfur (S), % 0 to 0.010
0 to 0.010