ASTM A372 Grade L Steel vs. EN 1.7177 Steel

Both ASTM A372 grade L steel and EN 1.7177 steel are iron alloys. They have a very high 98% of their average alloy composition in common. There are 25 material properties with values for both materials. Properties with values for just one material (6, in this case) are not shown.

For each property being compared, the top bar is ASTM A372 grade L steel and the bottom bar is EN 1.7177 steel.

Metric UnitsUS Customary Units

Mechanical Properties

Brinell Hardness 350
200 to 480
Elastic (Young's, Tensile) Modulus, GPa 190
190
Poisson's Ratio 0.29
0.29
Shear Modulus, GPa 73
73
Tensile Strength: Ultimate (UTS), MPa 1160
660 to 1990

Thermal Properties

Latent Heat of Fusion, J/g 250
250
Maximum Temperature: Mechanical, °C 430
420
Melting Completion (Liquidus), °C 1460
1450
Melting Onset (Solidus), °C 1420
1410
Specific Heat Capacity, J/kg-K 470
470
Thermal Conductivity, W/m-K 44
47
Thermal Expansion, µm/m-K 13
13

Electrical Properties

Electrical Conductivity: Equal Volume, % IACS 7.5
7.2
Electrical Conductivity: Equal Weight (Specific), % IACS 8.6
8.3

Otherwise Unclassified Properties

Base Metal Price, % relative 3.5
2.1
Density, g/cm3 7.8
7.8
Embodied Carbon, kg CO2/kg material 1.7
1.4
Embodied Energy, MJ/kg 22
19
Embodied Water, L/kg 54
49

Common Calculations

Stiffness to Weight: Axial, points 13
13
Stiffness to Weight: Bending, points 24
24
Strength to Weight: Axial, points 41
23 to 71
Strength to Weight: Bending, points 31
21 to 45
Thermal Diffusivity, mm2/s 12
13
Thermal Shock Resistance, points 34
19 to 59

Alloy Composition

Carbon (C), % 0.38 to 0.43
0.55 to 0.65
Chromium (Cr), % 0.7 to 0.9
0.6 to 0.9
Iron (Fe), % 95.2 to 96.3
97 to 98.2
Manganese (Mn), % 0.6 to 0.8
0.7 to 1.0
Molybdenum (Mo), % 0.2 to 0.3
0
Nickel (Ni), % 1.7 to 2.0
0
Phosphorus (P), % 0 to 0.015
0 to 0.025
Silicon (Si), % 0.15 to 0.35
0 to 0.4
Sulfur (S), % 0 to 0.010
0 to 0.025