ASTM A372 Grade L Steel vs. CC330G Bronze

ASTM A372 grade L steel belongs to the iron alloys classification, while CC330G bronze belongs to the copper alloys. There are 29 material properties with values for both materials. Properties with values for just one material (2, in this case) are not shown.

For each property being compared, the top bar is ASTM A372 grade L steel and the bottom bar is CC330G bronze.

Metric UnitsUS Customary Units

Mechanical Properties

Brinell Hardness 350
110
Elastic (Young's, Tensile) Modulus, GPa 190
110
Elongation at Break, % 14
20
Poisson's Ratio 0.29
0.34
Shear Modulus, GPa 73
42
Tensile Strength: Ultimate (UTS), MPa 1160
530
Tensile Strength: Yield (Proof), MPa 1040
190

Thermal Properties

Latent Heat of Fusion, J/g 250
230
Maximum Temperature: Mechanical, °C 430
220
Melting Completion (Liquidus), °C 1460
1050
Melting Onset (Solidus), °C 1420
1000
Specific Heat Capacity, J/kg-K 470
430
Thermal Conductivity, W/m-K 44
62
Thermal Expansion, µm/m-K 13
18

Electrical Properties

Electrical Conductivity: Equal Volume, % IACS 7.5
14
Electrical Conductivity: Equal Weight (Specific), % IACS 8.6
15

Otherwise Unclassified Properties

Base Metal Price, % relative 3.5
29
Density, g/cm3 7.8
8.4
Embodied Carbon, kg CO2/kg material 1.7
3.2
Embodied Energy, MJ/kg 22
52
Embodied Water, L/kg 54
390

Common Calculations

Resilience: Ultimate (Unit Rupture Work), MJ/m3 150
82
Resilience: Unit (Modulus of Resilience), kJ/m3 2890
170
Stiffness to Weight: Axial, points 13
7.5
Stiffness to Weight: Bending, points 24
19
Strength to Weight: Axial, points 41
18
Strength to Weight: Bending, points 31
17
Thermal Diffusivity, mm2/s 12
17
Thermal Shock Resistance, points 34
19

Alloy Composition

Aluminum (Al), % 0
8.0 to 10.5
Carbon (C), % 0.38 to 0.43
0
Chromium (Cr), % 0.7 to 0.9
0
Copper (Cu), % 0
87 to 92
Iron (Fe), % 95.2 to 96.3
0 to 1.2
Lead (Pb), % 0
0 to 0.3
Manganese (Mn), % 0.6 to 0.8
0 to 0.5
Molybdenum (Mo), % 0.2 to 0.3
0
Nickel (Ni), % 1.7 to 2.0
0 to 1.0
Phosphorus (P), % 0 to 0.015
0
Silicon (Si), % 0.15 to 0.35
0 to 0.2
Sulfur (S), % 0 to 0.010
0
Tin (Sn), % 0
0 to 0.3
Zinc (Zn), % 0
0 to 0.5