ASTM A372 Grade L Steel vs. R30003 Cobalt

ASTM A372 grade L steel belongs to the iron alloys classification, while R30003 cobalt belongs to the cobalt alloys. There are 27 material properties with values for both materials. Properties with values for just one material (4, in this case) are not shown.

For each property being compared, the top bar is ASTM A372 grade L steel and the bottom bar is R30003 cobalt.

Metric UnitsUS Customary Units

Mechanical Properties

Elastic (Young's, Tensile) Modulus, GPa 190
210
Elongation at Break, % 14
10 to 73
Fatigue Strength, MPa 670
320 to 560
Poisson's Ratio 0.29
0.29
Shear Modulus, GPa 73
83
Tensile Strength: Ultimate (UTS), MPa 1160
970 to 1720
Tensile Strength: Yield (Proof), MPa 1040
510 to 1090

Thermal Properties

Latent Heat of Fusion, J/g 250
310
Melting Completion (Liquidus), °C 1460
1400
Melting Onset (Solidus), °C 1420
1440
Specific Heat Capacity, J/kg-K 470
450
Thermal Conductivity, W/m-K 44
13
Thermal Expansion, µm/m-K 13
13

Electrical Properties

Electrical Conductivity: Equal Volume, % IACS 7.5
2.0
Electrical Conductivity: Equal Weight (Specific), % IACS 8.6
2.1

Otherwise Unclassified Properties

Base Metal Price, % relative 3.5
95
Density, g/cm3 7.8
8.4
Embodied Carbon, kg CO2/kg material 1.7
8.0
Embodied Energy, MJ/kg 22
110
Embodied Water, L/kg 54
400

Common Calculations

Resilience: Unit (Modulus of Resilience), kJ/m3 2890
600 to 2790
Stiffness to Weight: Axial, points 13
14
Stiffness to Weight: Bending, points 24
24
Strength to Weight: Axial, points 41
32 to 57
Strength to Weight: Bending, points 31
26 to 38
Thermal Diffusivity, mm2/s 12
3.3
Thermal Shock Resistance, points 34
26 to 45

Alloy Composition

Boron (B), % 0
0 to 0.1
Carbon (C), % 0.38 to 0.43
0 to 0.15
Chromium (Cr), % 0.7 to 0.9
19 to 21
Cobalt (Co), % 0
39 to 41
Iron (Fe), % 95.2 to 96.3
10 to 20.5
Manganese (Mn), % 0.6 to 0.8
1.5 to 2.5
Molybdenum (Mo), % 0.2 to 0.3
6.0 to 8.0
Nickel (Ni), % 1.7 to 2.0
14 to 16
Phosphorus (P), % 0 to 0.015
0 to 0.015
Silicon (Si), % 0.15 to 0.35
0 to 1.2
Sulfur (S), % 0 to 0.010
0 to 0.015