ASTM A387 Grade 11 Steel vs. AISI 301LN Stainless Steel

Both ASTM A387 grade 11 steel and AISI 301LN stainless steel are iron alloys. They have 77% of their average alloy composition in common. There are 32 material properties with values for both materials. Properties with values for just one material (1, in this case) are not shown.

For each property being compared, the top bar is ASTM A387 grade 11 steel and the bottom bar is AISI 301LN stainless steel.

Metric UnitsUS Customary Units

Mechanical Properties

Brinell Hardness 150 to 180
210 to 320
Elastic (Young's, Tensile) Modulus, GPa 190
200
Elongation at Break, % 25
23 to 51
Fatigue Strength, MPa 200 to 250
270 to 520
Poisson's Ratio 0.29
0.28
Shear Modulus, GPa 73
77
Shear Strength, MPa 320 to 390
450 to 670
Tensile Strength: Ultimate (UTS), MPa 500 to 600
630 to 1060
Tensile Strength: Yield (Proof), MPa 270 to 350
270 to 770

Thermal Properties

Latent Heat of Fusion, J/g 260
280
Maximum Temperature: Mechanical, °C 430
890
Melting Completion (Liquidus), °C 1460
1430
Melting Onset (Solidus), °C 1420
1380
Specific Heat Capacity, J/kg-K 470
480
Thermal Conductivity, W/m-K 39
15
Thermal Expansion, µm/m-K 13
16

Electrical Properties

Electrical Conductivity: Equal Volume, % IACS 7.4
2.4
Electrical Conductivity: Equal Weight (Specific), % IACS 8.5
2.7

Otherwise Unclassified Properties

Base Metal Price, % relative 2.9
13
Density, g/cm3 7.8
7.8
Embodied Carbon, kg CO2/kg material 1.6
2.7
Embodied Energy, MJ/kg 21
39
Embodied Water, L/kg 53
130

Common Calculations

PREN (Pitting Resistance) 3.1
19
Resilience: Ultimate (Unit Rupture Work), MJ/m3 100 to 130
220 to 290
Resilience: Unit (Modulus of Resilience), kJ/m3 200 to 320
180 to 1520
Stiffness to Weight: Axial, points 13
14
Stiffness to Weight: Bending, points 24
25
Strength to Weight: Axial, points 18 to 21
22 to 38
Strength to Weight: Bending, points 18 to 20
21 to 30
Thermal Diffusivity, mm2/s 11
4.0
Thermal Shock Resistance, points 15 to 18
14 to 24

Alloy Composition

Carbon (C), % 0.050 to 0.17
0 to 0.030
Chromium (Cr), % 1.0 to 1.5
16 to 18
Iron (Fe), % 96.2 to 97.6
70.7 to 77.9
Manganese (Mn), % 0.4 to 0.65
0 to 2.0
Molybdenum (Mo), % 0.45 to 0.65
0
Nickel (Ni), % 0
6.0 to 8.0
Nitrogen (N), % 0
0.070 to 0.2
Phosphorus (P), % 0 to 0.025
0 to 0.045
Silicon (Si), % 0.5 to 0.8
0 to 1.0
Sulfur (S), % 0 to 0.025
0 to 0.030

Comparable Variants