ASTM A387 Grade 11 Steel vs. AWS E219

Both ASTM A387 grade 11 steel and AWS E219 are iron alloys. They have 66% of their average alloy composition in common. There are 23 material properties with values for both materials. Properties with values for just one material (9, in this case) are not shown.

For each property being compared, the top bar is ASTM A387 grade 11 steel and the bottom bar is AWS E219.

Metric UnitsUS Customary Units

Mechanical Properties

Elastic (Young's, Tensile) Modulus, GPa 190
200
Elongation at Break, % 25
17
Poisson's Ratio 0.29
0.28
Shear Modulus, GPa 73
78
Tensile Strength: Ultimate (UTS), MPa 500 to 600
690

Thermal Properties

Latent Heat of Fusion, J/g 260
290
Melting Completion (Liquidus), °C 1460
1400
Melting Onset (Solidus), °C 1420
1360
Specific Heat Capacity, J/kg-K 470
480
Thermal Conductivity, W/m-K 39
14
Thermal Expansion, µm/m-K 13
15

Otherwise Unclassified Properties

Base Metal Price, % relative 2.9
15
Density, g/cm3 7.8
7.7
Embodied Carbon, kg CO2/kg material 1.6
3.1
Embodied Energy, MJ/kg 21
44
Embodied Water, L/kg 53
160

Common Calculations

PREN (Pitting Resistance) 3.1
25
Stiffness to Weight: Axial, points 13
14
Stiffness to Weight: Bending, points 24
25
Strength to Weight: Axial, points 18 to 21
25
Strength to Weight: Bending, points 18 to 20
23
Thermal Diffusivity, mm2/s 11
3.8
Thermal Shock Resistance, points 15 to 18
17

Alloy Composition

Carbon (C), % 0.050 to 0.17
0 to 0.060
Chromium (Cr), % 1.0 to 1.5
19 to 21.5
Copper (Cu), % 0
0 to 0.75
Iron (Fe), % 96.2 to 97.6
58.6 to 67.4
Manganese (Mn), % 0.4 to 0.65
8.0 to 10
Molybdenum (Mo), % 0.45 to 0.65
0 to 0.75
Nickel (Ni), % 0
5.5 to 7.0
Nitrogen (N), % 0
0.1 to 0.3
Phosphorus (P), % 0 to 0.025
0 to 0.040
Silicon (Si), % 0.5 to 0.8
0 to 1.0
Sulfur (S), % 0 to 0.025
0 to 0.030