ASTM A387 Grade 11 Steel vs. EN 1.1165 Cast Steel
Both ASTM A387 grade 11 steel and EN 1.1165 cast steel are iron alloys. They have a very high 98% of their average alloy composition in common. There are 29 material properties with values for both materials. Properties with values for just one material (4, in this case) are not shown.
For each property being compared, the top bar is ASTM A387 grade 11 steel and the bottom bar is EN 1.1165 cast steel.
Metric UnitsUS Customary Units
Mechanical Properties
| Elastic (Young's, Tensile) Modulus, GPa | 190 | |
| 190 |
| Elongation at Break, % | 25 | |
| 11 to 20 |
| Fatigue Strength, MPa | 200 to 250 | |
| 200 to 380 |
| Poisson's Ratio | 0.29 | |
| 0.29 |
| Shear Modulus, GPa | 73 | |
| 73 |
| Tensile Strength: Ultimate (UTS), MPa | 500 to 600 | |
| 600 to 780 |
| Tensile Strength: Yield (Proof), MPa | 270 to 350 | |
| 290 to 620 |
Thermal Properties
| Latent Heat of Fusion, J/g | 260 | |
| 250 |
| Maximum Temperature: Mechanical, °C | 430 | |
| 400 |
| Melting Completion (Liquidus), °C | 1460 | |
| 1460 |
| Melting Onset (Solidus), °C | 1420 | |
| 1420 |
| Specific Heat Capacity, J/kg-K | 470 | |
| 470 |
| Thermal Conductivity, W/m-K | 39 | |
| 51 |
| Thermal Expansion, µm/m-K | 13 | |
| 12 |
Electrical Properties
| Electrical Conductivity: Equal Volume, % IACS | 7.4 | |
| 7.8 |
| Electrical Conductivity: Equal Weight (Specific), % IACS | 8.5 | |
| 8.9 |
Otherwise Unclassified Properties
| Base Metal Price, % relative | 2.9 | |
| 1.9 |
| Density, g/cm3 | 7.8 | |
| 7.8 |
| Embodied Carbon, kg CO2/kg material | 1.6 | |
| 1.4 |
| Embodied Energy, MJ/kg | 21 | |
| 19 |
| Embodied Water, L/kg | 53 | |
| 47 |
Common Calculations
| Resilience: Ultimate (Unit Rupture Work), MJ/m3 | 100 to 130 | |
| 81 to 100 |
| Resilience: Unit (Modulus of Resilience), kJ/m3 | 200 to 320 | |
| 230 to 1010 |
| Stiffness to Weight: Axial, points | 13 | |
| 13 |
| Stiffness to Weight: Bending, points | 24 | |
| 24 |
| Strength to Weight: Axial, points | 18 to 21 | |
| 21 to 28 |
| Strength to Weight: Bending, points | 18 to 20 | |
| 20 to 24 |
| Thermal Diffusivity, mm2/s | 11 | |
| 14 |
| Thermal Shock Resistance, points | 15 to 18 | |
| 19 to 25 |
Alloy Composition
| Carbon (C), % | 0.050 to 0.17 | |
| 0.25 to 0.32 |
| Chromium (Cr), % | 1.0 to 1.5 | |
| 0 |
| Iron (Fe), % | 96.2 to 97.6 | |
| 97.2 to 98.6 |
| Manganese (Mn), % | 0.4 to 0.65 | |
| 1.2 to 1.8 |
| Molybdenum (Mo), % | 0.45 to 0.65 | |
| 0 |
| Phosphorus (P), % | 0 to 0.025 | |
| 0 to 0.035 |
| Silicon (Si), % | 0.5 to 0.8 | |
| 0 to 0.6 |
| Sulfur (S), % | 0 to 0.025 | |
| 0 to 0.030 |