ASTM A387 Grade 11 Steel vs. EN 1.4571 Stainless Steel

Both ASTM A387 grade 11 steel and EN 1.4571 stainless steel are iron alloys. They have 69% of their average alloy composition in common. There are 32 material properties with values for both materials. Properties with values for just one material (1, in this case) are not shown.

For each property being compared, the top bar is ASTM A387 grade 11 steel and the bottom bar is EN 1.4571 stainless steel.

Metric UnitsUS Customary Units

Mechanical Properties

Brinell Hardness 150 to 180
190 to 270
Elastic (Young's, Tensile) Modulus, GPa 190
200
Elongation at Break, % 25
14 to 40
Fatigue Strength, MPa 200 to 250
200 to 330
Poisson's Ratio 0.29
0.28
Shear Modulus, GPa 73
78
Shear Strength, MPa 320 to 390
410 to 550
Tensile Strength: Ultimate (UTS), MPa 500 to 600
600 to 900
Tensile Strength: Yield (Proof), MPa 270 to 350
230 to 570

Thermal Properties

Latent Heat of Fusion, J/g 260
290
Maximum Temperature: Mechanical, °C 430
950
Melting Completion (Liquidus), °C 1460
1440
Melting Onset (Solidus), °C 1420
1400
Specific Heat Capacity, J/kg-K 470
470
Thermal Conductivity, W/m-K 39
15
Thermal Expansion, µm/m-K 13
17

Electrical Properties

Electrical Conductivity: Equal Volume, % IACS 7.4
2.3
Electrical Conductivity: Equal Weight (Specific), % IACS 8.5
2.6

Otherwise Unclassified Properties

Base Metal Price, % relative 2.9
19
Density, g/cm3 7.8
7.9
Embodied Carbon, kg CO2/kg material 1.6
3.9
Embodied Energy, MJ/kg 21
54
Embodied Water, L/kg 53
150

Common Calculations

PREN (Pitting Resistance) 3.1
25
Resilience: Ultimate (Unit Rupture Work), MJ/m3 100 to 130
110 to 190
Resilience: Unit (Modulus of Resilience), kJ/m3 200 to 320
130 to 820
Stiffness to Weight: Axial, points 13
14
Stiffness to Weight: Bending, points 24
25
Strength to Weight: Axial, points 18 to 21
21 to 32
Strength to Weight: Bending, points 18 to 20
20 to 26
Thermal Diffusivity, mm2/s 11
4.0
Thermal Shock Resistance, points 15 to 18
13 to 20

Alloy Composition

Carbon (C), % 0.050 to 0.17
0 to 0.080
Chromium (Cr), % 1.0 to 1.5
16.5 to 18.5
Iron (Fe), % 96.2 to 97.6
61.7 to 71
Manganese (Mn), % 0.4 to 0.65
0 to 2.0
Molybdenum (Mo), % 0.45 to 0.65
2.0 to 2.5
Nickel (Ni), % 0
10.5 to 13.5
Phosphorus (P), % 0 to 0.025
0 to 0.045
Silicon (Si), % 0.5 to 0.8
0 to 1.0
Sulfur (S), % 0 to 0.025
0 to 0.015
Titanium (Ti), % 0
0 to 0.7

Comparable Variants