ASTM A387 Grade 11 Steel vs. EN 1.5503 Steel

Both ASTM A387 grade 11 steel and EN 1.5503 steel are iron alloys. They have a very high 98% of their average alloy composition in common. There are 31 material properties with values for both materials. Properties with values for just one material (2, in this case) are not shown.

For each property being compared, the top bar is ASTM A387 grade 11 steel and the bottom bar is EN 1.5503 steel.

Metric UnitsUS Customary Units

Mechanical Properties

Brinell Hardness 150 to 180
120 to 160
Elastic (Young's, Tensile) Modulus, GPa 190
190
Elongation at Break, % 25
12 to 17
Fatigue Strength, MPa 200 to 250
180 to 280
Poisson's Ratio 0.29
0.29
Shear Modulus, GPa 73
73
Shear Strength, MPa 320 to 390
270 to 320
Tensile Strength: Ultimate (UTS), MPa 500 to 600
400 to 520
Tensile Strength: Yield (Proof), MPa 270 to 350
270 to 430

Thermal Properties

Latent Heat of Fusion, J/g 260
250
Maximum Temperature: Mechanical, °C 430
400
Melting Completion (Liquidus), °C 1460
1460
Melting Onset (Solidus), °C 1420
1420
Specific Heat Capacity, J/kg-K 470
470
Thermal Conductivity, W/m-K 39
52
Thermal Expansion, µm/m-K 13
13

Electrical Properties

Electrical Conductivity: Equal Volume, % IACS 7.4
7.0
Electrical Conductivity: Equal Weight (Specific), % IACS 8.5
8.1

Otherwise Unclassified Properties

Base Metal Price, % relative 2.9
1.8
Density, g/cm3 7.8
7.8
Embodied Carbon, kg CO2/kg material 1.6
1.4
Embodied Energy, MJ/kg 21
18
Embodied Water, L/kg 53
46

Common Calculations

Resilience: Ultimate (Unit Rupture Work), MJ/m3 100 to 130
41 to 81
Resilience: Unit (Modulus of Resilience), kJ/m3 200 to 320
200 to 490
Stiffness to Weight: Axial, points 13
13
Stiffness to Weight: Bending, points 24
24
Strength to Weight: Axial, points 18 to 21
14 to 19
Strength to Weight: Bending, points 18 to 20
15 to 18
Thermal Diffusivity, mm2/s 11
14
Thermal Shock Resistance, points 15 to 18
12 to 15

Alloy Composition

Boron (B), % 0
0.00080 to 0.0050
Carbon (C), % 0.050 to 0.17
0.16 to 0.2
Chromium (Cr), % 1.0 to 1.5
0
Copper (Cu), % 0
0 to 0.25
Iron (Fe), % 96.2 to 97.6
98.4 to 99.239
Manganese (Mn), % 0.4 to 0.65
0.6 to 0.8
Molybdenum (Mo), % 0.45 to 0.65
0
Phosphorus (P), % 0 to 0.025
0 to 0.025
Silicon (Si), % 0.5 to 0.8
0 to 0.3
Sulfur (S), % 0 to 0.025
0 to 0.025