ASTM A387 Grade 11 Steel vs. CC331G Bronze

ASTM A387 grade 11 steel belongs to the iron alloys classification, while CC331G bronze belongs to the copper alloys. There are 29 material properties with values for both materials. Properties with values for just one material (3, in this case) are not shown.

For each property being compared, the top bar is ASTM A387 grade 11 steel and the bottom bar is CC331G bronze.

Metric UnitsUS Customary Units

Mechanical Properties

Brinell Hardness 150 to 180
140
Elastic (Young's, Tensile) Modulus, GPa 190
110
Elongation at Break, % 25
20
Poisson's Ratio 0.29
0.34
Shear Modulus, GPa 73
43
Tensile Strength: Ultimate (UTS), MPa 500 to 600
620
Tensile Strength: Yield (Proof), MPa 270 to 350
240

Thermal Properties

Latent Heat of Fusion, J/g 260
230
Maximum Temperature: Mechanical, °C 430
220
Melting Completion (Liquidus), °C 1460
1060
Melting Onset (Solidus), °C 1420
1000
Specific Heat Capacity, J/kg-K 470
440
Thermal Conductivity, W/m-K 39
61
Thermal Expansion, µm/m-K 13
18

Electrical Properties

Electrical Conductivity: Equal Volume, % IACS 7.4
13
Electrical Conductivity: Equal Weight (Specific), % IACS 8.5
14

Otherwise Unclassified Properties

Base Metal Price, % relative 2.9
28
Density, g/cm3 7.8
8.3
Embodied Carbon, kg CO2/kg material 1.6
3.2
Embodied Energy, MJ/kg 21
53
Embodied Water, L/kg 53
390

Common Calculations

Resilience: Ultimate (Unit Rupture Work), MJ/m3 100 to 130
97
Resilience: Unit (Modulus of Resilience), kJ/m3 200 to 320
250
Stiffness to Weight: Axial, points 13
7.6
Stiffness to Weight: Bending, points 24
19
Strength to Weight: Axial, points 18 to 21
21
Strength to Weight: Bending, points 18 to 20
19
Thermal Diffusivity, mm2/s 11
17
Thermal Shock Resistance, points 15 to 18
22

Alloy Composition

Aluminum (Al), % 0
8.5 to 10.5
Carbon (C), % 0.050 to 0.17
0
Chromium (Cr), % 1.0 to 1.5
0
Copper (Cu), % 0
83 to 86.5
Iron (Fe), % 96.2 to 97.6
1.5 to 3.5
Lead (Pb), % 0
0 to 0.1
Magnesium (Mg), % 0
0 to 0.050
Manganese (Mn), % 0.4 to 0.65
0 to 1.0
Molybdenum (Mo), % 0.45 to 0.65
0
Nickel (Ni), % 0
0 to 1.5
Phosphorus (P), % 0 to 0.025
0
Silicon (Si), % 0.5 to 0.8
0 to 0.2
Sulfur (S), % 0 to 0.025
0
Tin (Sn), % 0
0 to 0.2
Zinc (Zn), % 0
0 to 0.5