ASTM A387 Grade 11 Steel vs. C10800 Copper

ASTM A387 grade 11 steel belongs to the iron alloys classification, while C10800 copper belongs to the copper alloys. There are 29 material properties with values for both materials. Properties with values for just one material (6, in this case) are not shown.

For each property being compared, the top bar is ASTM A387 grade 11 steel and the bottom bar is C10800 copper.

Metric UnitsUS Customary Units

Mechanical Properties

Elastic (Young's, Tensile) Modulus, GPa 190
120
Elongation at Break, % 25
4.0 to 50
Poisson's Ratio 0.29
0.34
Shear Modulus, GPa 73
43
Shear Strength, MPa 320 to 390
150 to 200
Tensile Strength: Ultimate (UTS), MPa 500 to 600
220 to 380
Tensile Strength: Yield (Proof), MPa 270 to 350
75 to 370

Thermal Properties

Latent Heat of Fusion, J/g 260
210
Maximum Temperature: Mechanical, °C 430
200
Melting Completion (Liquidus), °C 1460
1080
Melting Onset (Solidus), °C 1420
1080
Specific Heat Capacity, J/kg-K 470
390
Thermal Conductivity, W/m-K 39
350
Thermal Expansion, µm/m-K 13
17

Electrical Properties

Electrical Conductivity: Equal Volume, % IACS 7.4
92
Electrical Conductivity: Equal Weight (Specific), % IACS 8.5
92

Otherwise Unclassified Properties

Base Metal Price, % relative 2.9
31
Density, g/cm3 7.8
9.0
Embodied Carbon, kg CO2/kg material 1.6
2.6
Embodied Energy, MJ/kg 21
41
Embodied Water, L/kg 53
310

Common Calculations

Resilience: Ultimate (Unit Rupture Work), MJ/m3 100 to 130
15 to 88
Resilience: Unit (Modulus of Resilience), kJ/m3 200 to 320
24 to 600
Stiffness to Weight: Axial, points 13
7.2
Stiffness to Weight: Bending, points 24
18
Strength to Weight: Axial, points 18 to 21
6.8 to 12
Strength to Weight: Bending, points 18 to 20
9.1 to 13
Thermal Diffusivity, mm2/s 11
100
Thermal Shock Resistance, points 15 to 18
7.8 to 13

Alloy Composition

Carbon (C), % 0.050 to 0.17
0
Chromium (Cr), % 1.0 to 1.5
0
Copper (Cu), % 0
99.95 to 99.995
Iron (Fe), % 96.2 to 97.6
0
Manganese (Mn), % 0.4 to 0.65
0
Molybdenum (Mo), % 0.45 to 0.65
0
Phosphorus (P), % 0 to 0.025
0.0050 to 0.012
Silicon (Si), % 0.5 to 0.8
0
Sulfur (S), % 0 to 0.025
0