ASTM A387 Grade 11 Steel vs. S35500 Stainless Steel

Both ASTM A387 grade 11 steel and S35500 stainless steel are iron alloys. They have 78% of their average alloy composition in common. There are 31 material properties with values for both materials. Properties with values for just one material (3, in this case) are not shown.

For each property being compared, the top bar is ASTM A387 grade 11 steel and the bottom bar is S35500 stainless steel.

Metric UnitsUS Customary Units

Mechanical Properties

Elastic (Young's, Tensile) Modulus, GPa 190
200
Elongation at Break, % 25
14
Fatigue Strength, MPa 200 to 250
690 to 730
Poisson's Ratio 0.29
0.28
Shear Modulus, GPa 73
78
Shear Strength, MPa 320 to 390
810 to 910
Tensile Strength: Ultimate (UTS), MPa 500 to 600
1330 to 1490
Tensile Strength: Yield (Proof), MPa 270 to 350
1200 to 1280

Thermal Properties

Latent Heat of Fusion, J/g 260
280
Maximum Temperature: Mechanical, °C 430
870
Melting Completion (Liquidus), °C 1460
1460
Melting Onset (Solidus), °C 1420
1420
Specific Heat Capacity, J/kg-K 470
470
Thermal Conductivity, W/m-K 39
16
Thermal Expansion, µm/m-K 13
11

Electrical Properties

Electrical Conductivity: Equal Volume, % IACS 7.4
2.2
Electrical Conductivity: Equal Weight (Specific), % IACS 8.5
2.5

Otherwise Unclassified Properties

Base Metal Price, % relative 2.9
16
Density, g/cm3 7.8
7.8
Embodied Carbon, kg CO2/kg material 1.6
3.5
Embodied Energy, MJ/kg 21
47
Embodied Water, L/kg 53
130

Common Calculations

PREN (Pitting Resistance) 3.1
27
Resilience: Ultimate (Unit Rupture Work), MJ/m3 100 to 130
180 to 190
Resilience: Unit (Modulus of Resilience), kJ/m3 200 to 320
3610 to 4100
Stiffness to Weight: Axial, points 13
14
Stiffness to Weight: Bending, points 24
25
Strength to Weight: Axial, points 18 to 21
47 to 53
Strength to Weight: Bending, points 18 to 20
34 to 37
Thermal Diffusivity, mm2/s 11
4.4
Thermal Shock Resistance, points 15 to 18
44 to 49

Alloy Composition

Carbon (C), % 0.050 to 0.17
0.1 to 0.15
Chromium (Cr), % 1.0 to 1.5
15 to 16
Iron (Fe), % 96.2 to 97.6
73.2 to 77.7
Manganese (Mn), % 0.4 to 0.65
0.5 to 1.3
Molybdenum (Mo), % 0.45 to 0.65
2.5 to 3.2
Nickel (Ni), % 0
4.0 to 5.0
Niobium (Nb), % 0
0.1 to 0.5
Nitrogen (N), % 0
0.070 to 0.13
Phosphorus (P), % 0 to 0.025
0 to 0.040
Silicon (Si), % 0.5 to 0.8
0 to 0.5
Sulfur (S), % 0 to 0.025
0 to 0.030

Comparable Variants