ASTM A387 Grade 12 Steel vs. ACI-ASTM CD6MN Steel

Both ASTM A387 grade 12 steel and ACI-ASTM CD6MN steel are iron alloys. They have 68% of their average alloy composition in common. There are 30 material properties with values for both materials. Properties with values for just one material (3, in this case) are not shown.

For each property being compared, the top bar is ASTM A387 grade 12 steel and the bottom bar is ACI-ASTM CD6MN steel.

Metric UnitsUS Customary Units

Mechanical Properties

Elastic (Young's, Tensile) Modulus, GPa 190
200
Elongation at Break, % 25
28
Fatigue Strength, MPa 190 to 230
370
Poisson's Ratio 0.29
0.27
Shear Modulus, GPa 73
80
Tensile Strength: Ultimate (UTS), MPa 470 to 520
730
Tensile Strength: Yield (Proof), MPa 260 to 310
510

Thermal Properties

Latent Heat of Fusion, J/g 250
300
Maximum Temperature: Mechanical, °C 430
1100
Melting Completion (Liquidus), °C 1470
1440
Melting Onset (Solidus), °C 1420
1390
Specific Heat Capacity, J/kg-K 470
480
Thermal Conductivity, W/m-K 44
16
Thermal Expansion, µm/m-K 13
13

Electrical Properties

Electrical Conductivity: Equal Volume, % IACS 7.2
2.1
Electrical Conductivity: Equal Weight (Specific), % IACS 8.3
2.4

Otherwise Unclassified Properties

Base Metal Price, % relative 2.8
17
Density, g/cm3 7.8
7.7
Embodied Carbon, kg CO2/kg material 1.6
3.4
Embodied Energy, MJ/kg 21
48
Embodied Water, L/kg 51
170

Common Calculations

PREN (Pitting Resistance) 2.7
36
Resilience: Ultimate (Unit Rupture Work), MJ/m3 98 to 110
180
Resilience: Unit (Modulus of Resilience), kJ/m3 180 to 250
650
Stiffness to Weight: Axial, points 13
15
Stiffness to Weight: Bending, points 24
25
Strength to Weight: Axial, points 16 to 18
26
Strength to Weight: Bending, points 17 to 18
23
Thermal Diffusivity, mm2/s 12
4.4
Thermal Shock Resistance, points 14 to 15
20

Alloy Composition

Carbon (C), % 0.050 to 0.17
0 to 0.060
Chromium (Cr), % 0.8 to 1.2
24 to 27
Iron (Fe), % 97 to 98.2
62.1 to 70.1
Manganese (Mn), % 0.4 to 0.65
0 to 1.0
Molybdenum (Mo), % 0.45 to 0.6
1.8 to 2.5
Nickel (Ni), % 0
4.0 to 6.0
Nitrogen (N), % 0
0.15 to 0.25
Phosphorus (P), % 0 to 0.025
0 to 0.040
Silicon (Si), % 0.15 to 0.4
0 to 1.0
Sulfur (S), % 0 to 0.025
0 to 0.040