ASTM A387 Grade 12 Steel vs. EN 1.4913 Stainless Steel

Both ASTM A387 grade 12 steel and EN 1.4913 stainless steel are iron alloys. They have 89% of their average alloy composition in common. There are 31 material properties with values for both materials. Properties with values for just one material (2, in this case) are not shown.

For each property being compared, the top bar is ASTM A387 grade 12 steel and the bottom bar is EN 1.4913 stainless steel.

Metric UnitsUS Customary Units

Mechanical Properties

Elastic (Young's, Tensile) Modulus, GPa 190
190
Elongation at Break, % 25
14 to 22
Fatigue Strength, MPa 190 to 230
320 to 480
Poisson's Ratio 0.29
0.28
Shear Modulus, GPa 73
75
Shear Strength, MPa 300 to 330
550 to 590
Tensile Strength: Ultimate (UTS), MPa 470 to 520
870 to 980
Tensile Strength: Yield (Proof), MPa 260 to 310
480 to 850

Thermal Properties

Latent Heat of Fusion, J/g 250
270
Maximum Temperature: Mechanical, °C 430
700
Melting Completion (Liquidus), °C 1470
1460
Melting Onset (Solidus), °C 1420
1410
Specific Heat Capacity, J/kg-K 470
480
Thermal Conductivity, W/m-K 44
24
Thermal Expansion, µm/m-K 13
11

Electrical Properties

Electrical Conductivity: Equal Volume, % IACS 7.2
2.9
Electrical Conductivity: Equal Weight (Specific), % IACS 8.3
3.3

Otherwise Unclassified Properties

Base Metal Price, % relative 2.8
9.0
Density, g/cm3 7.8
7.8
Embodied Carbon, kg CO2/kg material 1.6
2.9
Embodied Energy, MJ/kg 21
41
Embodied Water, L/kg 51
97

Common Calculations

PREN (Pitting Resistance) 2.7
14
Resilience: Ultimate (Unit Rupture Work), MJ/m3 98 to 110
130 to 160
Resilience: Unit (Modulus of Resilience), kJ/m3 180 to 250
600 to 1860
Stiffness to Weight: Axial, points 13
14
Stiffness to Weight: Bending, points 24
25
Strength to Weight: Axial, points 16 to 18
31 to 35
Strength to Weight: Bending, points 17 to 18
26 to 28
Thermal Diffusivity, mm2/s 12
6.5
Thermal Shock Resistance, points 14 to 15
31 to 34

Alloy Composition

Aluminum (Al), % 0
0 to 0.020
Boron (B), % 0
0 to 0.0015
Carbon (C), % 0.050 to 0.17
0.17 to 0.23
Chromium (Cr), % 0.8 to 1.2
10 to 11.5
Iron (Fe), % 97 to 98.2
84.5 to 88.3
Manganese (Mn), % 0.4 to 0.65
0.4 to 0.9
Molybdenum (Mo), % 0.45 to 0.6
0.5 to 0.8
Nickel (Ni), % 0
0.2 to 0.6
Niobium (Nb), % 0
0.25 to 0.55
Nitrogen (N), % 0
0.050 to 0.1
Phosphorus (P), % 0 to 0.025
0 to 0.025
Silicon (Si), % 0.15 to 0.4
0 to 0.5
Sulfur (S), % 0 to 0.025
0 to 0.015
Vanadium (V), % 0
0.1 to 0.3

Comparable Variants