ASTM A387 Grade 12 Steel vs. EN 1.4919 Stainless Steel

Both ASTM A387 grade 12 steel and EN 1.4919 stainless steel are iron alloys. They have 70% of their average alloy composition in common. There are 32 material properties with values for both materials. Properties with values for just one material (2, in this case) are not shown.

For each property being compared, the top bar is ASTM A387 grade 12 steel and the bottom bar is EN 1.4919 stainless steel.

Metric UnitsUS Customary Units

Mechanical Properties

Brinell Hardness 140 to 160
180
Elastic (Young's, Tensile) Modulus, GPa 190
200
Elongation at Break, % 25
40
Fatigue Strength, MPa 190 to 230
200
Poisson's Ratio 0.29
0.28
Shear Modulus, GPa 73
78
Shear Strength, MPa 300 to 330
400
Tensile Strength: Ultimate (UTS), MPa 470 to 520
590
Tensile Strength: Yield (Proof), MPa 260 to 310
230

Thermal Properties

Latent Heat of Fusion, J/g 250
290
Maximum Temperature: Mechanical, °C 430
950
Melting Completion (Liquidus), °C 1470
1440
Melting Onset (Solidus), °C 1420
1400
Specific Heat Capacity, J/kg-K 470
470
Thermal Conductivity, W/m-K 44
16
Thermal Expansion, µm/m-K 13
16

Electrical Properties

Electrical Conductivity: Equal Volume, % IACS 7.2
2.3
Electrical Conductivity: Equal Weight (Specific), % IACS 8.3
2.7

Otherwise Unclassified Properties

Base Metal Price, % relative 2.8
19
Density, g/cm3 7.8
7.9
Embodied Carbon, kg CO2/kg material 1.6
3.8
Embodied Energy, MJ/kg 21
52
Embodied Water, L/kg 51
150

Common Calculations

PREN (Pitting Resistance) 2.7
26
Resilience: Ultimate (Unit Rupture Work), MJ/m3 98 to 110
190
Resilience: Unit (Modulus of Resilience), kJ/m3 180 to 250
130
Stiffness to Weight: Axial, points 13
14
Stiffness to Weight: Bending, points 24
25
Strength to Weight: Axial, points 16 to 18
21
Strength to Weight: Bending, points 17 to 18
20
Thermal Diffusivity, mm2/s 12
4.3
Thermal Shock Resistance, points 14 to 15
13

Alloy Composition

Boron (B), % 0
0.0015 to 0.0050
Carbon (C), % 0.050 to 0.17
0.040 to 0.080
Chromium (Cr), % 0.8 to 1.2
16.5 to 18.5
Iron (Fe), % 97 to 98.2
62.8 to 71.5
Manganese (Mn), % 0.4 to 0.65
0 to 2.0
Molybdenum (Mo), % 0.45 to 0.6
2.0 to 2.5
Nickel (Ni), % 0
10 to 13
Nitrogen (N), % 0
0 to 0.1
Phosphorus (P), % 0 to 0.025
0 to 0.035
Silicon (Si), % 0.15 to 0.4
0 to 1.0
Sulfur (S), % 0 to 0.025
0 to 0.015