ASTM A387 Grade 12 Steel vs. N08020 Stainless Steel

Both ASTM A387 grade 12 steel and N08020 stainless steel are iron alloys. They have a modest 39% of their average alloy composition in common, which, by itself, doesn't mean much. There are 31 material properties with values for both materials. Properties with values for just one material (2, in this case) are not shown.

For each property being compared, the top bar is ASTM A387 grade 12 steel and the bottom bar is N08020 stainless steel.

Metric UnitsUS Customary Units

Mechanical Properties

Elastic (Young's, Tensile) Modulus, GPa 190
200
Elongation at Break, % 25
15 to 34
Fatigue Strength, MPa 190 to 230
210 to 240
Poisson's Ratio 0.29
0.28
Shear Modulus, GPa 73
77
Shear Strength, MPa 300 to 330
380 to 410
Tensile Strength: Ultimate (UTS), MPa 470 to 520
610 to 620
Tensile Strength: Yield (Proof), MPa 260 to 310
270 to 420

Thermal Properties

Latent Heat of Fusion, J/g 250
300
Maximum Temperature: Mechanical, °C 430
1100
Melting Completion (Liquidus), °C 1470
1410
Melting Onset (Solidus), °C 1420
1360
Specific Heat Capacity, J/kg-K 470
460
Thermal Conductivity, W/m-K 44
12
Thermal Expansion, µm/m-K 13
15

Electrical Properties

Electrical Conductivity: Equal Volume, % IACS 7.2
1.6
Electrical Conductivity: Equal Weight (Specific), % IACS 8.3
1.8

Otherwise Unclassified Properties

Base Metal Price, % relative 2.8
38
Density, g/cm3 7.8
8.2
Embodied Carbon, kg CO2/kg material 1.6
6.6
Embodied Energy, MJ/kg 21
92
Embodied Water, L/kg 51
220

Common Calculations

PREN (Pitting Resistance) 2.7
28
Resilience: Ultimate (Unit Rupture Work), MJ/m3 98 to 110
83 to 170
Resilience: Unit (Modulus of Resilience), kJ/m3 180 to 250
180 to 440
Stiffness to Weight: Axial, points 13
13
Stiffness to Weight: Bending, points 24
24
Strength to Weight: Axial, points 16 to 18
21
Strength to Weight: Bending, points 17 to 18
20
Thermal Diffusivity, mm2/s 12
3.2
Thermal Shock Resistance, points 14 to 15
15

Alloy Composition

Carbon (C), % 0.050 to 0.17
0 to 0.070
Chromium (Cr), % 0.8 to 1.2
19 to 21
Copper (Cu), % 0
3.0 to 4.0
Iron (Fe), % 97 to 98.2
29.9 to 44
Manganese (Mn), % 0.4 to 0.65
0 to 2.0
Molybdenum (Mo), % 0.45 to 0.6
2.0 to 3.0
Nickel (Ni), % 0
32 to 38
Niobium (Nb), % 0
0 to 1.0
Phosphorus (P), % 0 to 0.025
0 to 0.045
Silicon (Si), % 0.15 to 0.4
0 to 1.0
Sulfur (S), % 0 to 0.025
0 to 0.035