ASTM A387 Grade 12 Steel vs. N08801 Stainless Steel

Both ASTM A387 grade 12 steel and N08801 stainless steel are iron alloys. They have 47% of their average alloy composition in common. There are 31 material properties with values for both materials. Properties with values for just one material (2, in this case) are not shown.

For each property being compared, the top bar is ASTM A387 grade 12 steel and the bottom bar is N08801 stainless steel.

Metric UnitsUS Customary Units

Mechanical Properties

Elastic (Young's, Tensile) Modulus, GPa 190
200
Elongation at Break, % 25
34
Fatigue Strength, MPa 190 to 230
260
Poisson's Ratio 0.29
0.28
Shear Modulus, GPa 73
77
Shear Strength, MPa 300 to 330
570
Tensile Strength: Ultimate (UTS), MPa 470 to 520
860
Tensile Strength: Yield (Proof), MPa 260 to 310
190

Thermal Properties

Latent Heat of Fusion, J/g 250
300
Maximum Temperature: Mechanical, °C 430
1090
Melting Completion (Liquidus), °C 1470
1390
Melting Onset (Solidus), °C 1420
1360
Specific Heat Capacity, J/kg-K 470
480
Thermal Conductivity, W/m-K 44
12
Thermal Expansion, µm/m-K 13
16

Electrical Properties

Electrical Conductivity: Equal Volume, % IACS 7.2
1.7
Electrical Conductivity: Equal Weight (Specific), % IACS 8.3
1.9

Otherwise Unclassified Properties

Base Metal Price, % relative 2.8
30
Density, g/cm3 7.8
8.0
Embodied Carbon, kg CO2/kg material 1.6
5.5
Embodied Energy, MJ/kg 21
79
Embodied Water, L/kg 51
200

Common Calculations

PREN (Pitting Resistance) 2.7
21
Resilience: Ultimate (Unit Rupture Work), MJ/m3 98 to 110
220
Resilience: Unit (Modulus of Resilience), kJ/m3 180 to 250
92
Stiffness to Weight: Axial, points 13
14
Stiffness to Weight: Bending, points 24
24
Strength to Weight: Axial, points 16 to 18
30
Strength to Weight: Bending, points 17 to 18
25
Thermal Diffusivity, mm2/s 12
3.3
Thermal Shock Resistance, points 14 to 15
20

Alloy Composition

Carbon (C), % 0.050 to 0.17
0 to 0.1
Chromium (Cr), % 0.8 to 1.2
19 to 22
Copper (Cu), % 0
0 to 0.5
Iron (Fe), % 97 to 98.2
39.5 to 50.3
Manganese (Mn), % 0.4 to 0.65
0 to 1.5
Molybdenum (Mo), % 0.45 to 0.6
0
Nickel (Ni), % 0
30 to 34
Phosphorus (P), % 0 to 0.025
0
Silicon (Si), % 0.15 to 0.4
0 to 1.0
Sulfur (S), % 0 to 0.025
0 to 0.015
Titanium (Ti), % 0
0.75 to 1.5