ASTM A387 Grade 12 Steel vs. R04295 Alloy

ASTM A387 grade 12 steel belongs to the iron alloys classification, while R04295 alloy belongs to the otherwise unclassified metals. There are 18 material properties with values for both materials. Properties with values for just one material (14, in this case) are not shown.

For each property being compared, the top bar is ASTM A387 grade 12 steel and the bottom bar is R04295 alloy.

Metric UnitsUS Customary Units

Mechanical Properties

Elastic (Young's, Tensile) Modulus, GPa 190
100
Elongation at Break, % 25
22
Poisson's Ratio 0.29
0.38
Shear Modulus, GPa 73
37
Tensile Strength: Ultimate (UTS), MPa 470 to 520
410
Tensile Strength: Yield (Proof), MPa 260 to 310
300

Thermal Properties

Latent Heat of Fusion, J/g 250
300
Specific Heat Capacity, J/kg-K 470
260
Thermal Expansion, µm/m-K 13
7.2

Otherwise Unclassified Properties

Density, g/cm3 7.8
9.0
Embodied Water, L/kg 51
950

Common Calculations

Resilience: Ultimate (Unit Rupture Work), MJ/m3 98 to 110
84
Resilience: Unit (Modulus of Resilience), kJ/m3 180 to 250
430
Stiffness to Weight: Axial, points 13
6.3
Stiffness to Weight: Bending, points 24
17
Strength to Weight: Axial, points 16 to 18
13
Strength to Weight: Bending, points 17 to 18
14
Thermal Shock Resistance, points 14 to 15
40

Alloy Composition

Carbon (C), % 0.050 to 0.17
0 to 0.015
Chromium (Cr), % 0.8 to 1.2
0
Hafnium (Hf), % 0
9.0 to 11
Hydrogen (H), % 0
0 to 0.0015
Iron (Fe), % 97 to 98.2
0
Manganese (Mn), % 0.4 to 0.65
0
Molybdenum (Mo), % 0.45 to 0.6
0
Niobium (Nb), % 0
85.9 to 90.3
Nitrogen (N), % 0
0 to 0.010
Oxygen (O), % 0
0 to 0.025
Phosphorus (P), % 0 to 0.025
0
Silicon (Si), % 0.15 to 0.4
0
Sulfur (S), % 0 to 0.025
0
Tantalum (Ta), % 0
0 to 0.5
Titanium (Ti), % 0
0.7 to 1.3
Tungsten (W), % 0
0 to 0.5
Zirconium (Zr), % 0
0 to 0.7