ASTM A387 Grade 2 Steel vs. R58150 Titanium
ASTM A387 grade 2 steel belongs to the iron alloys classification, while R58150 titanium belongs to the titanium alloys. There are 26 material properties with values for both materials. Properties with values for just one material (7, in this case) are not shown.
For each property being compared, the top bar is ASTM A387 grade 2 steel and the bottom bar is R58150 titanium.
Metric UnitsUS Customary Units
Mechanical Properties
| Elastic (Young's, Tensile) Modulus, GPa | 190 | |
| 140 |
| Elongation at Break, % | 25 | |
| 13 |
| Fatigue Strength, MPa | 190 to 250 | |
| 330 |
| Poisson's Ratio | 0.29 | |
| 0.32 |
| Shear Modulus, GPa | 73 | |
| 52 |
| Shear Strength, MPa | 300 to 350 | |
| 470 |
| Tensile Strength: Ultimate (UTS), MPa | 470 to 550 | |
| 770 |
| Tensile Strength: Yield (Proof), MPa | 260 to 350 | |
| 550 |
Thermal Properties
| Latent Heat of Fusion, J/g | 250 | |
| 410 |
| Maximum Temperature: Mechanical, °C | 420 | |
| 320 |
| Melting Completion (Liquidus), °C | 1470 | |
| 1760 |
| Melting Onset (Solidus), °C | 1420 | |
| 1700 |
| Specific Heat Capacity, J/kg-K | 470 | |
| 500 |
| Thermal Expansion, µm/m-K | 13 | |
| 8.4 |
Otherwise Unclassified Properties
| Base Metal Price, % relative | 2.6 | |
| 48 |
| Density, g/cm3 | 7.9 | |
| 5.4 |
| Embodied Carbon, kg CO2/kg material | 1.6 | |
| 31 |
| Embodied Energy, MJ/kg | 20 | |
| 480 |
| Embodied Water, L/kg | 50 | |
| 150 |
Common Calculations
| Resilience: Ultimate (Unit Rupture Work), MJ/m3 | 98 to 120 | |
| 94 |
| Resilience: Unit (Modulus of Resilience), kJ/m3 | 180 to 320 | |
| 1110 |
| Stiffness to Weight: Axial, points | 13 | |
| 14 |
| Stiffness to Weight: Bending, points | 24 | |
| 32 |
| Strength to Weight: Axial, points | 16 to 20 | |
| 40 |
| Strength to Weight: Bending, points | 17 to 19 | |
| 35 |
| Thermal Shock Resistance, points | 14 to 16 | |
| 48 |
Alloy Composition
| Carbon (C), % | 0.050 to 0.21 | |
| 0 to 0.1 |
| Chromium (Cr), % | 0.5 to 0.8 | |
| 0 |
| Hydrogen (H), % | 0 | |
| 0 to 0.015 |
| Iron (Fe), % | 97.1 to 98.3 | |
| 0 to 0.1 |
| Manganese (Mn), % | 0.55 to 0.8 | |
| 0 |
| Molybdenum (Mo), % | 0.45 to 0.6 | |
| 14 to 16 |
| Nitrogen (N), % | 0 | |
| 0 to 0.050 |
| Oxygen (O), % | 0 | |
| 0 to 0.2 |
| Phosphorus (P), % | 0 to 0.025 | |
| 0 |
| Silicon (Si), % | 0.15 to 0.4 | |
| 0 |
| Sulfur (S), % | 0 to 0.025 | |
| 0 |
| Titanium (Ti), % | 0 | |
| 83.5 to 86 |