ASTM A387 Grade 21L Class 1 vs. EN 1.0558 Cast Steel

Both ASTM A387 grade 21L class 1 and EN 1.0558 cast steel are iron alloys. They have a very high 95% of their average alloy composition in common. There are 29 material properties with values for both materials. Properties with values for just one material (4, in this case) are not shown.

For each property being compared, the top bar is ASTM A387 grade 21L class 1 and the bottom bar is EN 1.0558 cast steel.

Metric UnitsUS Customary Units

Mechanical Properties

Elastic (Young's, Tensile) Modulus, GPa 190
190
Elongation at Break, % 21
18
Fatigue Strength, MPa 160
230
Poisson's Ratio 0.29
0.29
Shear Modulus, GPa 74
73
Tensile Strength: Ultimate (UTS), MPa 500
640
Tensile Strength: Yield (Proof), MPa 230
340

Thermal Properties

Latent Heat of Fusion, J/g 260
250
Maximum Temperature: Mechanical, °C 480
400
Melting Completion (Liquidus), °C 1470
1470
Melting Onset (Solidus), °C 1430
1430
Specific Heat Capacity, J/kg-K 470
470
Thermal Conductivity, W/m-K 41
53
Thermal Expansion, µm/m-K 13
12

Electrical Properties

Electrical Conductivity: Equal Volume, % IACS 7.6
7.8
Electrical Conductivity: Equal Weight (Specific), % IACS 8.8
8.9

Otherwise Unclassified Properties

Base Metal Price, % relative 4.1
1.7
Density, g/cm3 7.9
7.9
Embodied Carbon, kg CO2/kg material 1.8
1.4
Embodied Energy, MJ/kg 23
18
Embodied Water, L/kg 62
45

Common Calculations

Resilience: Ultimate (Unit Rupture Work), MJ/m3 84
99
Resilience: Unit (Modulus of Resilience), kJ/m3 140
300
Stiffness to Weight: Axial, points 13
13
Stiffness to Weight: Bending, points 24
24
Strength to Weight: Axial, points 18
22
Strength to Weight: Bending, points 18
21
Thermal Diffusivity, mm2/s 11
14
Thermal Shock Resistance, points 14
20

Alloy Composition

Carbon (C), % 0 to 0.1
0
Chromium (Cr), % 2.8 to 3.3
0
Iron (Fe), % 94.4 to 96.1
99.935 to 100
Manganese (Mn), % 0.3 to 0.6
0
Molybdenum (Mo), % 0.9 to 1.1
0
Phosphorus (P), % 0 to 0.025
0 to 0.035
Silicon (Si), % 0 to 0.5
0
Sulfur (S), % 0 to 0.025
0 to 0.030