ASTM A387 Grade 9 Steel vs. C66100 Bronze
ASTM A387 grade 9 steel belongs to the iron alloys classification, while C66100 bronze belongs to the copper alloys. There are 27 material properties with values for both materials. Properties with values for just one material (5, in this case) are not shown.
For each property being compared, the top bar is ASTM A387 grade 9 steel and the bottom bar is C66100 bronze.
Metric UnitsUS Customary Units
Mechanical Properties
| Elastic (Young's, Tensile) Modulus, GPa | 190 | |
| 120 |
| Elongation at Break, % | 20 to 21 | |
| 8.0 to 40 |
| Poisson's Ratio | 0.28 | |
| 0.34 |
| Shear Modulus, GPa | 75 | |
| 43 |
| Shear Strength, MPa | 310 to 380 | |
| 280 to 460 |
| Tensile Strength: Ultimate (UTS), MPa | 500 to 600 | |
| 410 to 790 |
| Tensile Strength: Yield (Proof), MPa | 230 to 350 | |
| 120 to 430 |
Thermal Properties
| Latent Heat of Fusion, J/g | 270 | |
| 260 |
| Maximum Temperature: Mechanical, °C | 600 | |
| 200 |
| Melting Completion (Liquidus), °C | 1460 | |
| 1050 |
| Melting Onset (Solidus), °C | 1410 | |
| 1000 |
| Specific Heat Capacity, J/kg-K | 470 | |
| 400 |
| Thermal Conductivity, W/m-K | 26 | |
| 34 |
| Thermal Expansion, µm/m-K | 13 | |
| 17 |
Otherwise Unclassified Properties
| Base Metal Price, % relative | 6.5 | |
| 29 |
| Density, g/cm3 | 7.8 | |
| 8.7 |
| Embodied Carbon, kg CO2/kg material | 2.1 | |
| 2.6 |
| Embodied Energy, MJ/kg | 28 | |
| 42 |
| Embodied Water, L/kg | 87 | |
| 300 |
Common Calculations
| Resilience: Ultimate (Unit Rupture Work), MJ/m3 | 83 to 110 | |
| 53 to 120 |
| Resilience: Unit (Modulus of Resilience), kJ/m3 | 140 to 310 | |
| 60 to 790 |
| Stiffness to Weight: Axial, points | 14 | |
| 7.4 |
| Stiffness to Weight: Bending, points | 25 | |
| 19 |
| Strength to Weight: Axial, points | 18 to 21 | |
| 13 to 25 |
| Strength to Weight: Bending, points | 18 to 20 | |
| 14 to 22 |
| Thermal Diffusivity, mm2/s | 6.9 | |
| 9.7 |
| Thermal Shock Resistance, points | 14 to 17 | |
| 15 to 29 |
Alloy Composition
Deprecated: Automatic conversion of false to array is deprecated in /home/public/compare.php on line 460
| Carbon (C), % | 0 to 0.15 | |
| 0 |
| Chromium (Cr), % | 8.0 to 10 | |
| 0 |
| Copper (Cu), % | 0 | |
| 92 to 97 |
| Iron (Fe), % | 87.1 to 90.8 | |
| 0 to 0.25 |
| Lead (Pb), % | 0 | |
| 0.2 to 0.8 |
| Manganese (Mn), % | 0.3 to 0.6 | |
| 0 to 1.5 |
| Molybdenum (Mo), % | 0.9 to 1.1 | |
| 0 |
| Phosphorus (P), % | 0 to 0.025 | |
| 0 |
| Silicon (Si), % | 0 to 1.0 | |
| 2.8 to 3.5 |
| Sulfur (S), % | 0 to 0.025 | |
| 0 |
| Vanadium (V), % | 0 to 0.040 | |
| 0 |
| Zinc (Zn), % | 0 | |
| 0 to 1.5 |
| Residuals, % | 0 | |
| 0 to 0.5 |