ASTM A387 Grade 9 Steel vs. ZA-8
ASTM A387 grade 9 steel belongs to the iron alloys classification, while ZA-8 belongs to the zinc alloys. There are 31 material properties with values for both materials. Properties with values for just one material (6, in this case) are not shown.
For each property being compared, the top bar is ASTM A387 grade 9 steel and the bottom bar is ZA-8.
Metric UnitsUS Customary Units
Mechanical Properties
| Brinell Hardness | 150 to 180 | |
| 87 to 100 |
| Elastic (Young's, Tensile) Modulus, GPa | 190 | |
| 85 to 86 |
| Elongation at Break, % | 20 to 21 | |
| 1.3 to 8.0 |
| Fatigue Strength, MPa | 160 to 240 | |
| 51 to 100 |
| Poisson's Ratio | 0.28 | |
| 0.26 |
| Shear Modulus, GPa | 75 | |
| 34 |
| Shear Strength, MPa | 310 to 380 | |
| 240 to 280 |
| Tensile Strength: Ultimate (UTS), MPa | 500 to 600 | |
| 210 to 370 |
| Tensile Strength: Yield (Proof), MPa | 230 to 350 | |
| 210 to 290 |
Thermal Properties
| Latent Heat of Fusion, J/g | 270 | |
| 110 |
| Maximum Temperature: Mechanical, °C | 600 | |
| 100 |
| Melting Completion (Liquidus), °C | 1460 | |
| 400 |
| Melting Onset (Solidus), °C | 1410 | |
| 380 |
| Specific Heat Capacity, J/kg-K | 470 | |
| 440 |
| Thermal Conductivity, W/m-K | 26 | |
| 120 |
| Thermal Expansion, µm/m-K | 13 | |
| 23 |
Electrical Properties
| Electrical Conductivity: Equal Volume, % IACS | 9.0 | |
| 28 |
| Electrical Conductivity: Equal Weight (Specific), % IACS | 10 | |
| 40 |
Otherwise Unclassified Properties
| Base Metal Price, % relative | 6.5 | |
| 11 |
| Density, g/cm3 | 7.8 | |
| 6.3 |
| Embodied Carbon, kg CO2/kg material | 2.1 | |
| 3.3 |
| Embodied Energy, MJ/kg | 28 | |
| 62 |
| Embodied Water, L/kg | 87 | |
| 420 |
Common Calculations
| Resilience: Ultimate (Unit Rupture Work), MJ/m3 | 83 to 110 | |
| 2.8 to 28 |
| Resilience: Unit (Modulus of Resilience), kJ/m3 | 140 to 310 | |
| 260 to 490 |
| Stiffness to Weight: Axial, points | 14 | |
| 7.5 |
| Stiffness to Weight: Bending, points | 25 | |
| 23 |
| Strength to Weight: Axial, points | 18 to 21 | |
| 9.3 to 17 |
| Strength to Weight: Bending, points | 18 to 20 | |
| 12 to 18 |
| Thermal Diffusivity, mm2/s | 6.9 | |
| 42 |
| Thermal Shock Resistance, points | 14 to 17 | |
| 7.6 to 13 |
Alloy Composition
| Aluminum (Al), % | 0 | |
| 8.0 to 8.8 |
| Cadmium (Cd), % | 0 | |
| 0 to 0.0060 |
| Carbon (C), % | 0 to 0.15 | |
| 0 |
| Chromium (Cr), % | 8.0 to 10 | |
| 0 |
| Copper (Cu), % | 0 | |
| 0.8 to 1.3 |
| Iron (Fe), % | 87.1 to 90.8 | |
| 0 to 0.075 |
| Lead (Pb), % | 0 | |
| 0 to 0.0060 |
| Magnesium (Mg), % | 0 | |
| 0.015 to 0.030 |
| Manganese (Mn), % | 0.3 to 0.6 | |
| 0 |
| Molybdenum (Mo), % | 0.9 to 1.1 | |
| 0 |
| Nickel (Ni), % | 0 | |
| 0 to 0.020 |
| Phosphorus (P), % | 0 to 0.025 | |
| 0 |
| Silicon (Si), % | 0 to 1.0 | |
| 0 to 0.045 |
| Sulfur (S), % | 0 to 0.025 | |
| 0 |
| Tin (Sn), % | 0 | |
| 0 to 0.0030 |
| Vanadium (V), % | 0 to 0.040 | |
| 0 |
| Zinc (Zn), % | 0 | |
| 89.7 to 91.2 |