ASTM A414 Steel vs. 88-silver 12-tin-oxide
ASTM A414 steel belongs to the iron alloys classification, while 88-silver 12-tin-oxide belongs to the otherwise unclassified metals. There are 6 material properties with values for both materials. Properties with values for just one material (25, in this case) are not shown.
For each property being compared, the top bar is ASTM A414 steel and the bottom bar is 88-silver 12-tin-oxide.
Metric UnitsUS Customary Units
Material Properties
| Electrical Conductivity: Equal Volume, % IACS | 7.2 to 7.3 | |
| 84 to 86 |
| Elongation at Break, % | 15 to 26 | |
| 9.0 to 37 |
| Resilience: Ultimate (Unit Rupture Work), MJ/m3 | 69 to 130 | |
| 24 to 70 |
| Shear Strength, MPa | 230 to 370 | |
| 150 to 160 |
| Tensile Strength: Ultimate (UTS), MPa | 360 to 590 | |
| 230 to 280 |
| Tensile Strength: Yield (Proof), MPa | 190 to 350 | |
| 110 to 260 |