ASTM A414 Steel vs. ACI-ASTM CD3MN Steel

Both ASTM A414 steel and ACI-ASTM CD3MN steel are iron alloys. There are 29 material properties with values for both materials. Properties with values for just one material (4, in this case) are not shown.

For each property being compared, the top bar is ASTM A414 steel and the bottom bar is ACI-ASTM CD3MN steel.

Metric UnitsUS Customary Units

Mechanical Properties

Elastic (Young's, Tensile) Modulus, GPa 190
200
Elongation at Break, % 15 to 26
29
Fatigue Strength, MPa 140 to 260
340
Poisson's Ratio 0.29
0.27
Shear Modulus, GPa 73
79
Tensile Strength: Ultimate (UTS), MPa 360 to 590
710
Tensile Strength: Yield (Proof), MPa 190 to 350
460

Thermal Properties

Latent Heat of Fusion, J/g 250
300
Maximum Temperature: Mechanical, °C 400
1060
Melting Completion (Liquidus), °C 1460
1450
Melting Onset (Solidus), °C 1420
1400
Specific Heat Capacity, J/kg-K 470
480
Thermal Conductivity, W/m-K 49 to 50
16
Thermal Expansion, µm/m-K 13
13

Electrical Properties

Electrical Conductivity: Equal Volume, % IACS 7.2 to 7.3
2.2
Electrical Conductivity: Equal Weight (Specific), % IACS 8.3 to 8.4
2.5

Otherwise Unclassified Properties

Base Metal Price, % relative 2.2
18
Density, g/cm3 7.8 to 7.9
7.8
Embodied Carbon, kg CO2/kg material 1.5 to 1.6
3.6
Embodied Energy, MJ/kg 20 to 22
50
Embodied Water, L/kg 48
160

Common Calculations

Resilience: Ultimate (Unit Rupture Work), MJ/m3 69 to 130
180
Resilience: Unit (Modulus of Resilience), kJ/m3 100 to 330
530
Stiffness to Weight: Axial, points 13
14
Stiffness to Weight: Bending, points 24
25
Strength to Weight: Axial, points 13 to 21
25
Strength to Weight: Bending, points 14 to 20
23
Thermal Diffusivity, mm2/s 13
4.3
Thermal Shock Resistance, points 11 to 17
20