ASTM A414 Steel vs. AISI 201 Stainless Steel

Both ASTM A414 steel and AISI 201 stainless steel are iron alloys. There are 31 material properties with values for both materials. Properties with values for just one material (2, in this case) are not shown.

For each property being compared, the top bar is ASTM A414 steel and the bottom bar is AISI 201 stainless steel.

Metric UnitsUS Customary Units

Mechanical Properties

Brinell Hardness 110 to 180
200 to 440
Elastic (Young's, Tensile) Modulus, GPa 190
200
Elongation at Break, % 15 to 26
4.6 to 51
Fatigue Strength, MPa 140 to 260
280 to 600
Poisson's Ratio 0.29
0.28
Shear Modulus, GPa 73
77
Shear Strength, MPa 230 to 370
450 to 840
Tensile Strength: Ultimate (UTS), MPa 360 to 590
650 to 1450
Tensile Strength: Yield (Proof), MPa 190 to 350
300 to 1080

Thermal Properties

Latent Heat of Fusion, J/g 250
280
Maximum Temperature: Mechanical, °C 400
880
Melting Completion (Liquidus), °C 1460
1410
Melting Onset (Solidus), °C 1420
1370
Specific Heat Capacity, J/kg-K 470
480
Thermal Conductivity, W/m-K 49 to 50
15
Thermal Expansion, µm/m-K 13
17

Electrical Properties

Electrical Conductivity: Equal Volume, % IACS 7.2 to 7.3
2.5
Electrical Conductivity: Equal Weight (Specific), % IACS 8.3 to 8.4
2.9

Otherwise Unclassified Properties

Base Metal Price, % relative 2.2
12
Density, g/cm3 7.8 to 7.9
7.7
Embodied Carbon, kg CO2/kg material 1.5 to 1.6
2.6
Embodied Energy, MJ/kg 20 to 22
38
Embodied Water, L/kg 48
140

Common Calculations

Resilience: Ultimate (Unit Rupture Work), MJ/m3 69 to 130
61 to 340
Resilience: Unit (Modulus of Resilience), kJ/m3 100 to 330
230 to 2970
Stiffness to Weight: Axial, points 13
14
Stiffness to Weight: Bending, points 24
25
Strength to Weight: Axial, points 13 to 21
23 to 52
Strength to Weight: Bending, points 14 to 20
22 to 37
Thermal Diffusivity, mm2/s 13
4.0
Thermal Shock Resistance, points 11 to 17
14 to 32