ASTM A414 Steel vs. AISI 440B Stainless Steel

Both ASTM A414 steel and AISI 440B stainless steel are iron alloys. There are 29 material properties with values for both materials. Properties with values for just one material (4, in this case) are not shown.

For each property being compared, the top bar is ASTM A414 steel and the bottom bar is AISI 440B stainless steel.

Metric UnitsUS Customary Units

Mechanical Properties

Elastic (Young's, Tensile) Modulus, GPa 190
200
Elongation at Break, % 15 to 26
3.0 to 18
Fatigue Strength, MPa 140 to 260
260 to 850
Poisson's Ratio 0.29
0.28
Shear Modulus, GPa 73
77
Shear Strength, MPa 230 to 370
460 to 1110
Tensile Strength: Ultimate (UTS), MPa 360 to 590
740 to 1930
Tensile Strength: Yield (Proof), MPa 190 to 350
430 to 1860

Thermal Properties

Latent Heat of Fusion, J/g 250
280
Maximum Temperature: Mechanical, °C 400
870
Melting Completion (Liquidus), °C 1460
1480
Melting Onset (Solidus), °C 1420
1370
Specific Heat Capacity, J/kg-K 470
480
Thermal Conductivity, W/m-K 49 to 50
23
Thermal Expansion, µm/m-K 13
10

Electrical Properties

Electrical Conductivity: Equal Volume, % IACS 7.2 to 7.3
2.5
Electrical Conductivity: Equal Weight (Specific), % IACS 8.3 to 8.4
2.9

Otherwise Unclassified Properties

Base Metal Price, % relative 2.2
9.0
Density, g/cm3 7.8 to 7.9
7.7
Embodied Carbon, kg CO2/kg material 1.5 to 1.6
2.2
Embodied Energy, MJ/kg 20 to 22
31
Embodied Water, L/kg 48
120

Common Calculations

Resilience: Ultimate (Unit Rupture Work), MJ/m3 69 to 130
57 to 110
Stiffness to Weight: Axial, points 13
14
Stiffness to Weight: Bending, points 24
25
Strength to Weight: Axial, points 13 to 21
27 to 70
Strength to Weight: Bending, points 14 to 20
24 to 45
Thermal Diffusivity, mm2/s 13
6.1
Thermal Shock Resistance, points 11 to 17
27 to 70