ASTM A414 Steel vs. Grade 364 Molybdenum
ASTM A414 steel belongs to the iron alloys classification, while grade 364 molybdenum belongs to the otherwise unclassified metals. There are 20 material properties with values for both materials. Properties with values for just one material (11, in this case) are not shown.
For each property being compared, the top bar is ASTM A414 steel and the bottom bar is grade 364 molybdenum.
Metric UnitsUS Customary Units
Mechanical Properties
| Elastic (Young's, Tensile) Modulus, GPa | 190 | |
| 310 |
| Elongation at Break, % | 15 to 26 | |
| 6.2 to 11 |
| Poisson's Ratio | 0.29 | |
| 0.31 |
| Shear Modulus, GPa | 73 | |
| 120 |
| Tensile Strength: Ultimate (UTS), MPa | 360 to 590 | |
| 580 to 720 |
| Tensile Strength: Yield (Proof), MPa | 190 to 350 | |
| 350 to 620 |
Thermal Properties
| Latent Heat of Fusion, J/g | 250 | |
| 370 |
| Specific Heat Capacity, J/kg-K | 470 | |
| 250 |
| Thermal Expansion, µm/m-K | 13 | |
| 7.0 |
Otherwise Unclassified Properties
| Density, g/cm3 | 7.8 to 7.9 | |
| 10 |
| Embodied Carbon, kg CO2/kg material | 1.5 to 1.6 | |
| 28 |
| Embodied Energy, MJ/kg | 20 to 22 | |
| 330 |
| Embodied Water, L/kg | 48 | |
| 360 |
Common Calculations
| Resilience: Ultimate (Unit Rupture Work), MJ/m3 | 69 to 130 | |
| 43 to 57 |
| Resilience: Unit (Modulus of Resilience), kJ/m3 | 100 to 330 | |
| 200 to 630 |
| Stiffness to Weight: Axial, points | 13 | |
| 17 |
| Stiffness to Weight: Bending, points | 24 | |
| 22 |
| Strength to Weight: Axial, points | 13 to 21 | |
| 16 to 20 |
| Strength to Weight: Bending, points | 14 to 20 | |
| 15 to 17 |
| Thermal Shock Resistance, points | 11 to 17 | |
| 19 to 24 |