ASTM A414 Steel vs. Grade FDSiCr Steel

Both ASTM A414 steel and grade FDSiCr steel are iron alloys. There are 25 material properties with values for both materials. Properties with values for just one material (7, in this case) are not shown.

For each property being compared, the top bar is ASTM A414 steel and the bottom bar is grade FDSiCr steel.

Metric UnitsUS Customary Units

Mechanical Properties

Brinell Hardness 110 to 180
580
Elastic (Young's, Tensile) Modulus, GPa 190
190
Poisson's Ratio 0.29
0.29
Shear Modulus, GPa 73
80
Tensile Strength: Ultimate (UTS), MPa 360 to 590
1930

Thermal Properties

Latent Heat of Fusion, J/g 250
270
Maximum Temperature: Mechanical, °C 400
410
Melting Completion (Liquidus), °C 1460
1440
Melting Onset (Solidus), °C 1420
1400
Specific Heat Capacity, J/kg-K 470
480
Thermal Conductivity, W/m-K 49 to 50
48
Thermal Expansion, µm/m-K 13
13

Electrical Properties

Electrical Conductivity: Equal Volume, % IACS 7.2 to 7.3
7.3
Electrical Conductivity: Equal Weight (Specific), % IACS 8.3 to 8.4
8.5

Otherwise Unclassified Properties

Base Metal Price, % relative 2.2
2.2
Density, g/cm3 7.8 to 7.9
7.7
Embodied Carbon, kg CO2/kg material 1.5 to 1.6
1.5
Embodied Energy, MJ/kg 20 to 22
20
Embodied Water, L/kg 48
48

Common Calculations

Stiffness to Weight: Axial, points 13
13
Stiffness to Weight: Bending, points 24
25
Strength to Weight: Axial, points 13 to 21
69
Strength to Weight: Bending, points 14 to 20
44
Thermal Diffusivity, mm2/s 13
13
Thermal Shock Resistance, points 11 to 17
58