ASTM A414 Steel vs. S44626 Stainless Steel

Both ASTM A414 steel and S44626 stainless steel are iron alloys. There are 31 material properties with values for both materials. Properties with values for just one material (3, in this case) are not shown.

For each property being compared, the top bar is ASTM A414 steel and the bottom bar is S44626 stainless steel.

Metric UnitsUS Customary Units

Mechanical Properties

Brinell Hardness 110 to 180
190
Elastic (Young's, Tensile) Modulus, GPa 190
200
Elongation at Break, % 15 to 26
23
Fatigue Strength, MPa 140 to 260
230
Poisson's Ratio 0.29
0.27
Shear Modulus, GPa 73
80
Shear Strength, MPa 230 to 370
340
Tensile Strength: Ultimate (UTS), MPa 360 to 590
540
Tensile Strength: Yield (Proof), MPa 190 to 350
350

Thermal Properties

Latent Heat of Fusion, J/g 250
300
Maximum Temperature: Mechanical, °C 400
1100
Melting Completion (Liquidus), °C 1460
1440
Melting Onset (Solidus), °C 1420
1390
Specific Heat Capacity, J/kg-K 470
480
Thermal Conductivity, W/m-K 49 to 50
17
Thermal Expansion, µm/m-K 13
11

Electrical Properties

Electrical Conductivity: Equal Volume, % IACS 7.2 to 7.3
2.3
Electrical Conductivity: Equal Weight (Specific), % IACS 8.3 to 8.4
2.7

Otherwise Unclassified Properties

Base Metal Price, % relative 2.2
14
Density, g/cm3 7.8 to 7.9
7.7
Embodied Carbon, kg CO2/kg material 1.5 to 1.6
2.9
Embodied Energy, MJ/kg 20 to 22
42
Embodied Water, L/kg 48
160

Common Calculations

Resilience: Ultimate (Unit Rupture Work), MJ/m3 69 to 130
110
Resilience: Unit (Modulus of Resilience), kJ/m3 100 to 330
300
Stiffness to Weight: Axial, points 13
15
Stiffness to Weight: Bending, points 24
26
Strength to Weight: Axial, points 13 to 21
19
Strength to Weight: Bending, points 14 to 20
19
Thermal Diffusivity, mm2/s 13
4.6
Thermal Shock Resistance, points 11 to 17
18