ASTM A514 Steel vs. ASTM A387 Grade 5 Steel
Both ASTM A514 steel and ASTM A387 grade 5 steel are iron alloys. There are 31 material properties with values for both materials. Properties with values for just one material (1, in this case) are not shown.
For each property being compared, the top bar is ASTM A514 steel and the bottom bar is ASTM A387 grade 5 steel.
Metric UnitsUS Customary Units
Mechanical Properties
| Brinell Hardness | 240 to 250 | |
| 150 to 180 |
| Elastic (Young's, Tensile) Modulus, GPa | 190 | |
| 190 |
| Elongation at Break, % | 18 to 21 | |
| 20 to 21 |
| Fatigue Strength, MPa | 470 to 540 | |
| 160 to 240 |
| Poisson's Ratio | 0.29 | |
| 0.29 |
| Shear Modulus, GPa | 73 | |
| 74 |
| Shear Strength, MPa | 490 to 520 | |
| 310 to 380 |
| Tensile Strength: Ultimate (UTS), MPa | 790 to 830 | |
| 500 to 600 |
| Tensile Strength: Yield (Proof), MPa | 690 to 770 | |
| 230 to 350 |
Thermal Properties
| Latent Heat of Fusion, J/g | 250 to 260 | |
| 260 |
| Maximum Temperature: Mechanical, °C | 400 to 440 | |
| 510 |
| Melting Completion (Liquidus), °C | 1460 | |
| 1460 |
| Melting Onset (Solidus), °C | 1420 | |
| 1420 |
| Specific Heat Capacity, J/kg-K | 470 | |
| 470 |
| Thermal Conductivity, W/m-K | 37 to 51 | |
| 40 |
| Thermal Expansion, µm/m-K | 13 | |
| 13 |
Electrical Properties
| Electrical Conductivity: Equal Volume, % IACS | 7.2 to 7.6 | |
| 8.0 |
| Electrical Conductivity: Equal Weight (Specific), % IACS | 8.3 to 8.8 | |
| 9.2 |
Otherwise Unclassified Properties
| Base Metal Price, % relative | 2.3 to 3.8 | |
| 4.3 |
| Density, g/cm3 | 7.8 to 7.9 | |
| 7.8 |
| Embodied Carbon, kg CO2/kg material | 1.6 to 1.8 | |
| 1.7 |
| Embodied Energy, MJ/kg | 21 to 25 | |
| 23 |
| Embodied Water, L/kg | 48 to 57 | |
| 69 |
Common Calculations
| Resilience: Ultimate (Unit Rupture Work), MJ/m3 | 140 to 170 | |
| 83 to 110 |
| Resilience: Unit (Modulus of Resilience), kJ/m3 | 1280 to 1590 | |
| 140 to 320 |
| Stiffness to Weight: Axial, points | 13 | |
| 14 |
| Stiffness to Weight: Bending, points | 24 | |
| 25 |
| Strength to Weight: Axial, points | 28 to 29 | |
| 18 to 21 |
| Strength to Weight: Bending, points | 24 to 25 | |
| 18 to 20 |
| Thermal Diffusivity, mm2/s | 10 to 14 | |
| 11 |
| Thermal Shock Resistance, points | 23 to 24 | |
| 14 to 17 |