ASTM A588 Steel vs. ACI-ASTM CN3M Steel

Both ASTM A588 steel and ACI-ASTM CN3M steel are iron alloys. There are 30 material properties with values for both materials. Properties with values for just one material (3, in this case) are not shown.

For each property being compared, the top bar is ASTM A588 steel and the bottom bar is ACI-ASTM CN3M steel.

Metric UnitsUS Customary Units

Mechanical Properties

Brinell Hardness 170
140
Elastic (Young's, Tensile) Modulus, GPa 190
200
Elongation at Break, % 22
34
Fatigue Strength, MPa 270
150
Poisson's Ratio 0.29
0.28
Shear Modulus, GPa 73
80
Tensile Strength: Ultimate (UTS), MPa 550
500
Tensile Strength: Yield (Proof), MPa 390
190

Thermal Properties

Latent Heat of Fusion, J/g 250 to 260
310
Maximum Temperature: Mechanical, °C 410
1100
Melting Completion (Liquidus), °C 1460
1450
Melting Onset (Solidus), °C 1410 to 1420
1400
Specific Heat Capacity, J/kg-K 470
470
Thermal Conductivity, W/m-K 43 to 44
13
Thermal Expansion, µm/m-K 13
16

Electrical Properties

Electrical Conductivity: Equal Volume, % IACS 7.4
1.7
Electrical Conductivity: Equal Weight (Specific), % IACS 8.5
1.9

Otherwise Unclassified Properties

Base Metal Price, % relative 2.3 to 2.5
31
Density, g/cm3 7.8
8.1
Embodied Carbon, kg CO2/kg material 1.5 to 1.6
5.9
Embodied Energy, MJ/kg 20 to 22
80
Embodied Water, L/kg 50 to 51
200

Common Calculations

Resilience: Ultimate (Unit Rupture Work), MJ/m3 110
130
Resilience: Unit (Modulus of Resilience), kJ/m3 400
89
Stiffness to Weight: Axial, points 13
14
Stiffness to Weight: Bending, points 24
24
Strength to Weight: Axial, points 20
17
Strength to Weight: Bending, points 19
17
Thermal Diffusivity, mm2/s 12
3.4
Thermal Shock Resistance, points 16
11