ASTM A588 Steel vs. EN 1.4729 Stainless Steel

Both ASTM A588 steel and EN 1.4729 stainless steel are iron alloys. There are 22 material properties with values for both materials. Properties with values for just one material (11, in this case) are not shown.

For each property being compared, the top bar is ASTM A588 steel and the bottom bar is EN 1.4729 stainless steel.

Metric UnitsUS Customary Units

Mechanical Properties

Brinell Hardness 170
260
Elastic (Young's, Tensile) Modulus, GPa 190
190
Elongation at Break, % 22
15
Poisson's Ratio 0.29
0.28
Shear Modulus, GPa 73
75

Thermal Properties

Latent Heat of Fusion, J/g 250 to 260
300
Maximum Temperature: Mechanical, °C 410
850
Melting Completion (Liquidus), °C 1460
1420
Melting Onset (Solidus), °C 1410 to 1420
1380
Specific Heat Capacity, J/kg-K 470
490
Thermal Conductivity, W/m-K 43 to 44
24
Thermal Expansion, µm/m-K 13
10

Electrical Properties

Electrical Conductivity: Equal Volume, % IACS 7.4
2.8
Electrical Conductivity: Equal Weight (Specific), % IACS 8.5
3.3

Otherwise Unclassified Properties

Base Metal Price, % relative 2.3 to 2.5
7.5
Density, g/cm3 7.8
7.6
Embodied Carbon, kg CO2/kg material 1.5 to 1.6
2.1
Embodied Energy, MJ/kg 20 to 22
29
Embodied Water, L/kg 50 to 51
100

Common Calculations

Stiffness to Weight: Axial, points 13
14
Stiffness to Weight: Bending, points 24
25
Thermal Diffusivity, mm2/s 12
6.5