ASTM A732 Cast Steel vs. SAE-AISI H25 Steel
Both ASTM A732 cast steel and SAE-AISI H25 steel are iron alloys. There are 21 material properties with values for both materials. Properties with values for just one material (10, in this case) are not shown.
For each property being compared, the top bar is ASTM A732 cast steel and the bottom bar is SAE-AISI H25 steel.
Metric UnitsUS Customary Units
Mechanical Properties
| Elastic (Young's, Tensile) Modulus, GPa | 190 | |
| 200 |
| Poisson's Ratio | 0.29 | |
| 0.29 |
| Shear Modulus, GPa | 72 to 73 | |
| 79 |
| Tensile Strength: Ultimate (UTS), MPa | 460 to 1470 | |
| 710 to 1620 |
Thermal Properties
| Latent Heat of Fusion, J/g | 250 to 260 | |
| 250 |
| Melting Completion (Liquidus), °C | 1440 to 1460 | |
| 1750 |
| Melting Onset (Solidus), °C | 1400 to 1420 | |
| 1700 |
| Specific Heat Capacity, J/kg-K | 470 to 480 | |
| 420 |
| Thermal Conductivity, W/m-K | 39 to 50 | |
| 26 |
| Thermal Expansion, µm/m-K | 13 | |
| 12 |
Otherwise Unclassified Properties
| Base Metal Price, % relative | 2.0 to 3.8 | |
| 38 |
| Density, g/cm3 | 7.8 to 7.9 | |
| 9.1 |
| Embodied Carbon, kg CO2/kg material | 1.4 to 1.7 | |
| 6.2 |
| Embodied Energy, MJ/kg | 19 to 24 | |
| 93 |
| Embodied Water, L/kg | 47 to 54 | |
| 83 |
Common Calculations
| Stiffness to Weight: Axial, points | 13 | |
| 12 |
| Stiffness to Weight: Bending, points | 24 | |
| 22 |
| Strength to Weight: Axial, points | 16 to 52 | |
| 22 to 50 |
| Strength to Weight: Bending, points | 17 to 37 | |
| 20 to 34 |
| Thermal Diffusivity, mm2/s | 10 to 14 | |
| 6.7 |
| Thermal Shock Resistance, points | 14 to 43 | |
| 22 to 49 |