ASTM B477 Au-Ni-Ag vs. 85-platinum 15-iridium
Both ASTM B477 Au-Ni-Ag and 85-platinum 15-iridium are otherwise unclassified metals. There are 19 material properties with values for both materials. Properties with values for just one material (1, in this case) are not shown.
For each property being compared, the top bar is ASTM B477 Au-Ni-Ag and the bottom bar is 85-platinum 15-iridium.
Metric UnitsUS Customary Units
Mechanical Properties
Elastic (Young's, Tensile) Modulus, GPa | 95 | |
220 |
Elongation at Break, % | 5.5 to 11 | |
5.5 to 34 |
Poisson's Ratio | 0.41 | |
0.38 |
Shear Modulus, GPa | 34 | |
81 |
Shear Strength, MPa | 190 to 320 | |
370 to 420 |
Tensile Strength: Ultimate (UTS), MPa | 310 to 550 | |
560 to 730 |
Thermal Properties
Latent Heat of Fusion, J/g | 80 | |
110 |
Melting Completion (Liquidus), °C | 1010 | |
1820 |
Melting Onset (Solidus), °C | 930 | |
1790 |
Specific Heat Capacity, J/kg-K | 160 | |
130 |
Thermal Expansion, µm/m-K | 15 | |
8.4 |
Electrical Properties
Electrical Conductivity: Equal Volume, % IACS | 14 | |
6.2 |
Electrical Conductivity: Equal Weight (Specific), % IACS | 7.5 | |
2.6 |
Otherwise Unclassified Properties
Density, g/cm3 | 17 | |
22 |
Common Calculations
Stiffness to Weight: Axial, points | 3.1 | |
5.7 |
Stiffness to Weight: Bending, points | 8.9 | |
9.3 |
Strength to Weight: Axial, points | 5.0 to 9.0 | |
7.1 to 9.3 |
Strength to Weight: Bending, points | 6.0 to 8.8 | |
6.9 to 8.3 |
Thermal Shock Resistance, points | 16 to 28 | |
21 to 28 |
Alloy Composition
Gold (Au), % | 74.2 to 75.8 | |
0 |
Iridium (Ir), % | 0 | |
14.5 to 15.5 |
Nickel (Ni), % | 2.6 to 3.4 | |
0 |
Platinum (Pt), % | 0 | |
84.3 to 85.5 |
Silver (Ag), % | 21.4 to 22.6 | |
0 |
Residuals, % | 0 | |
0 to 0.2 |