ASTM B477 Au-Ni-Ag vs. ASTM B541 Gold
Both ASTM B477 Au-Ni-Ag and ASTM B541 gold are otherwise unclassified metals. They have 76% of their average alloy composition in common. There are 20 material properties with values for both materials. Properties with values for just one material (3, in this case) are not shown.
For each property being compared, the top bar is ASTM B477 Au-Ni-Ag and the bottom bar is ASTM B541 gold.
Metric UnitsUS Customary Units
Mechanical Properties
| Elastic (Young's, Tensile) Modulus, GPa | 95 | |
| 110 |
| Elongation at Break, % | 5.5 to 11 | |
| 6.0 to 14 |
| Knoop Hardness | 100 to 190 | |
| 220 to 340 |
| Poisson's Ratio | 0.41 | |
| 0.4 |
| Shear Modulus, GPa | 34 | |
| 38 |
| Shear Strength, MPa | 190 to 320 | |
| 410 to 690 |
| Tensile Strength: Ultimate (UTS), MPa | 310 to 550 | |
| 670 to 1180 |
Thermal Properties
| Latent Heat of Fusion, J/g | 80 | |
| 90 |
| Melting Completion (Liquidus), °C | 1010 | |
| 1110 |
| Melting Onset (Solidus), °C | 930 | |
| 930 |
| Specific Heat Capacity, J/kg-K | 160 | |
| 170 |
| Thermal Expansion, µm/m-K | 15 | |
| 13 |
Electrical Properties
| Electrical Conductivity: Equal Volume, % IACS | 14 | |
| 7.7 to 12 |
| Electrical Conductivity: Equal Weight (Specific), % IACS | 7.5 | |
| 4.0 to 6.2 |
Otherwise Unclassified Properties
| Density, g/cm3 | 17 | |
| 17 |
Common Calculations
| Stiffness to Weight: Axial, points | 3.1 | |
| 3.4 |
| Stiffness to Weight: Bending, points | 8.9 | |
| 9.0 |
| Strength to Weight: Axial, points | 5.0 to 9.0 | |
| 11 to 19 |
| Strength to Weight: Bending, points | 6.0 to 8.8 | |
| 9.8 to 14 |
| Thermal Shock Resistance, points | 16 to 28 | |
| 36 to 63 |
Alloy Composition
Deprecated: Automatic conversion of false to array is deprecated in /home/public/compare.php on line 452
| Copper (Cu), % | 0 | |
| 13.5 to 15.5 |
| Gold (Au), % | 74.2 to 75.8 | |
| 70.5 to 72.5 |
| Nickel (Ni), % | 2.6 to 3.4 | |
| 0 |
| Platinum (Pt), % | 0 | |
| 8.0 to 9.0 |
| Silver (Ag), % | 21.4 to 22.6 | |
| 4.0 to 5.0 |
| Zinc (Zn), % | 0 | |
| 0.7 to 1.3 |
| Residuals, % | 0 to 0.3 | |
| 0 to 0.4 |