ASTM B477 Au-Ni-Ag vs. C17510 Copper
ASTM B477 Au-Ni-Ag belongs to the otherwise unclassified metals classification, while C17510 copper belongs to the copper alloys. There are 19 material properties with values for both materials. Properties with values for just one material (12, in this case) are not shown.
For each property being compared, the top bar is ASTM B477 Au-Ni-Ag and the bottom bar is C17510 copper.
Metric UnitsUS Customary Units
Mechanical Properties
| Elastic (Young's, Tensile) Modulus, GPa | 95 | |
| 120 |
| Elongation at Break, % | 5.5 to 11 | |
| 5.4 to 37 |
| Poisson's Ratio | 0.41 | |
| 0.34 |
| Shear Modulus, GPa | 34 | |
| 44 |
| Shear Strength, MPa | 190 to 320 | |
| 210 to 500 |
| Tensile Strength: Ultimate (UTS), MPa | 310 to 550 | |
| 310 to 860 |
Thermal Properties
| Latent Heat of Fusion, J/g | 80 | |
| 220 |
| Melting Completion (Liquidus), °C | 1010 | |
| 1070 |
| Melting Onset (Solidus), °C | 930 | |
| 1030 |
| Specific Heat Capacity, J/kg-K | 160 | |
| 390 |
| Thermal Expansion, µm/m-K | 15 | |
| 17 |
Electrical Properties
| Electrical Conductivity: Equal Volume, % IACS | 14 | |
| 22 to 54 |
| Electrical Conductivity: Equal Weight (Specific), % IACS | 7.5 | |
| 23 to 54 |
Otherwise Unclassified Properties
| Density, g/cm3 | 17 | |
| 8.9 |
Common Calculations
| Stiffness to Weight: Axial, points | 3.1 | |
| 7.4 |
| Stiffness to Weight: Bending, points | 8.9 | |
| 18 |
| Strength to Weight: Axial, points | 5.0 to 9.0 | |
| 9.7 to 27 |
| Strength to Weight: Bending, points | 6.0 to 8.8 | |
| 11 to 23 |
| Thermal Shock Resistance, points | 16 to 28 | |
| 11 to 30 |
Alloy Composition
Deprecated: Automatic conversion of false to array is deprecated in /home/public/compare.php on line 452
| Aluminum (Al), % | 0 | |
| 0 to 0.2 |
| Beryllium (Be), % | 0 | |
| 0.2 to 0.6 |
| Cobalt (Co), % | 0 | |
| 0 to 0.3 |
| Copper (Cu), % | 0 | |
| 95.9 to 98.4 |
| Gold (Au), % | 74.2 to 75.8 | |
| 0 |
| Iron (Fe), % | 0 | |
| 0 to 0.1 |
| Nickel (Ni), % | 2.6 to 3.4 | |
| 1.4 to 2.2 |
| Silicon (Si), % | 0 | |
| 0 to 0.2 |
| Silver (Ag), % | 21.4 to 22.6 | |
| 0 |
| Residuals, % | 0 to 0.3 | |
| 0 to 0.5 |