ASTM B540 Palladium vs. ASTM A387 Grade 12 Steel
ASTM B540 palladium belongs to the otherwise unclassified metals classification, while ASTM A387 grade 12 steel belongs to the iron alloys. There are 23 material properties with values for both materials. Properties with values for just one material (10, in this case) are not shown.
For each property being compared, the top bar is ASTM B540 palladium and the bottom bar is ASTM A387 grade 12 steel.
Metric UnitsUS Customary Units
Mechanical Properties
| Elastic (Young's, Tensile) Modulus, GPa | 110 | |
| 190 |
| Elongation at Break, % | 1.1 to 14 | |
| 25 |
| Fatigue Strength, MPa | 350 | |
| 190 to 230 |
| Poisson's Ratio | 0.38 | |
| 0.29 |
| Shear Modulus, GPa | 39 | |
| 73 |
| Shear Strength, MPa | 500 to 700 | |
| 300 to 330 |
| Tensile Strength: Ultimate (UTS), MPa | 830 to 1240 | |
| 470 to 520 |
| Tensile Strength: Yield (Proof), MPa | 620 to 1000 | |
| 260 to 310 |
Thermal Properties
| Latent Heat of Fusion, J/g | 140 | |
| 250 |
| Melting Completion (Liquidus), °C | 1220 | |
| 1470 |
| Melting Onset (Solidus), °C | 1020 | |
| 1420 |
| Specific Heat Capacity, J/kg-K | 240 | |
| 470 |
| Thermal Expansion, µm/m-K | 14 | |
| 13 |
Electrical Properties
| Electrical Conductivity: Equal Volume, % IACS | 4.9 to 5.5 | |
| 7.2 |
| Electrical Conductivity: Equal Weight (Specific), % IACS | 3.5 to 3.9 | |
| 8.3 |
Otherwise Unclassified Properties
| Density, g/cm3 | 13 | |
| 7.8 |
Common Calculations
| Resilience: Ultimate (Unit Rupture Work), MJ/m3 | 13 to 100 | |
| 98 to 110 |
| Resilience: Unit (Modulus of Resilience), kJ/m3 | 1790 to 4660 | |
| 180 to 250 |
| Stiffness to Weight: Axial, points | 4.7 | |
| 13 |
| Stiffness to Weight: Bending, points | 12 | |
| 24 |
| Strength to Weight: Axial, points | 18 to 27 | |
| 16 to 18 |
| Strength to Weight: Bending, points | 15 to 20 | |
| 17 to 18 |
| Thermal Shock Resistance, points | 41 to 61 | |
| 14 to 15 |
Alloy Composition
Deprecated: Automatic conversion of false to array is deprecated in /home/public/compare.php on line 452
| Carbon (C), % | 0 | |
| 0.050 to 0.17 |
| Chromium (Cr), % | 0 | |
| 0.8 to 1.2 |
| Copper (Cu), % | 13.5 to 14.5 | |
| 0 |
| Gold (Au), % | 9.5 to 10.5 | |
| 0 |
| Iron (Fe), % | 0 | |
| 97 to 98.2 |
| Manganese (Mn), % | 0 | |
| 0.4 to 0.65 |
| Molybdenum (Mo), % | 0 | |
| 0.45 to 0.6 |
| Palladium (Pd), % | 34 to 36 | |
| 0 |
| Phosphorus (P), % | 0 | |
| 0 to 0.025 |
| Platinum (Pt), % | 9.5 to 10.5 | |
| 0 |
| Silicon (Si), % | 0 | |
| 0.15 to 0.4 |
| Silver (Ag), % | 29 to 31 | |
| 0 |
| Sulfur (S), % | 0 | |
| 0 to 0.025 |
| Zinc (Zn), % | 0.8 to 1.2 | |
| 0 |
| Residuals, % | 0 to 0.3 | |
| 0 |