ASTM B540 Palladium vs. EN 1.4662 Stainless Steel
ASTM B540 palladium belongs to the otherwise unclassified metals classification, while EN 1.4662 stainless steel belongs to the iron alloys. There are 23 material properties with values for both materials. Properties with values for just one material (10, in this case) are not shown.
For each property being compared, the top bar is ASTM B540 palladium and the bottom bar is EN 1.4662 stainless steel.
Metric UnitsUS Customary Units
Mechanical Properties
| Elastic (Young's, Tensile) Modulus, GPa | 110 | |
| 200 |
| Elongation at Break, % | 1.1 to 14 | |
| 28 |
| Fatigue Strength, MPa | 350 | |
| 430 to 450 |
| Poisson's Ratio | 0.38 | |
| 0.27 |
| Shear Modulus, GPa | 39 | |
| 79 |
| Shear Strength, MPa | 500 to 700 | |
| 520 to 540 |
| Tensile Strength: Ultimate (UTS), MPa | 830 to 1240 | |
| 810 to 830 |
| Tensile Strength: Yield (Proof), MPa | 620 to 1000 | |
| 580 to 620 |
Thermal Properties
| Latent Heat of Fusion, J/g | 140 | |
| 290 |
| Melting Completion (Liquidus), °C | 1220 | |
| 1430 |
| Melting Onset (Solidus), °C | 1020 | |
| 1380 |
| Specific Heat Capacity, J/kg-K | 240 | |
| 480 |
| Thermal Expansion, µm/m-K | 14 | |
| 13 |
Electrical Properties
| Electrical Conductivity: Equal Volume, % IACS | 4.9 to 5.5 | |
| 2.2 |
| Electrical Conductivity: Equal Weight (Specific), % IACS | 3.5 to 3.9 | |
| 2.5 |
Otherwise Unclassified Properties
| Density, g/cm3 | 13 | |
| 7.7 |
Common Calculations
| Resilience: Ultimate (Unit Rupture Work), MJ/m3 | 13 to 100 | |
| 210 |
| Resilience: Unit (Modulus of Resilience), kJ/m3 | 1790 to 4660 | |
| 840 to 940 |
| Stiffness to Weight: Axial, points | 4.7 | |
| 15 |
| Stiffness to Weight: Bending, points | 12 | |
| 25 |
| Strength to Weight: Axial, points | 18 to 27 | |
| 29 to 30 |
| Strength to Weight: Bending, points | 15 to 20 | |
| 25 |
| Thermal Shock Resistance, points | 41 to 61 | |
| 22 |
Alloy Composition
Deprecated: Automatic conversion of false to array is deprecated in /home/public/compare.php on line 452
| Carbon (C), % | 0 | |
| 0 to 0.030 |
| Chromium (Cr), % | 0 | |
| 23 to 25 |
| Copper (Cu), % | 13.5 to 14.5 | |
| 0.1 to 0.8 |
| Gold (Au), % | 9.5 to 10.5 | |
| 0 |
| Iron (Fe), % | 0 | |
| 62.6 to 70.2 |
| Manganese (Mn), % | 0 | |
| 2.5 to 4.0 |
| Molybdenum (Mo), % | 0 | |
| 1.0 to 2.0 |
| Nickel (Ni), % | 0 | |
| 3.0 to 4.5 |
| Nitrogen (N), % | 0 | |
| 0.2 to 0.3 |
| Palladium (Pd), % | 34 to 36 | |
| 0 |
| Phosphorus (P), % | 0 | |
| 0 to 0.035 |
| Platinum (Pt), % | 9.5 to 10.5 | |
| 0 |
| Silicon (Si), % | 0 | |
| 0 to 0.7 |
| Silver (Ag), % | 29 to 31 | |
| 0 |
| Sulfur (S), % | 0 | |
| 0 to 0.0050 |
| Zinc (Zn), % | 0.8 to 1.2 | |
| 0 |
| Residuals, % | 0 to 0.3 | |
| 0 |