ASTM B540 Palladium vs. C66700 Brass
ASTM B540 palladium belongs to the otherwise unclassified metals classification, while C66700 brass belongs to the copper alloys. There are 22 material properties with values for both materials. Properties with values for just one material (11, in this case) are not shown.
For each property being compared, the top bar is ASTM B540 palladium and the bottom bar is C66700 brass.
Metric UnitsUS Customary Units
Mechanical Properties
| Elastic (Young's, Tensile) Modulus, GPa | 110 | |
| 110 |
| Elongation at Break, % | 1.1 to 14 | |
| 2.0 to 58 |
| Poisson's Ratio | 0.38 | |
| 0.31 |
| Shear Modulus, GPa | 39 | |
| 41 |
| Shear Strength, MPa | 500 to 700 | |
| 250 to 530 |
| Tensile Strength: Ultimate (UTS), MPa | 830 to 1240 | |
| 340 to 690 |
| Tensile Strength: Yield (Proof), MPa | 620 to 1000 | |
| 100 to 640 |
Thermal Properties
| Latent Heat of Fusion, J/g | 140 | |
| 180 |
| Melting Completion (Liquidus), °C | 1220 | |
| 1090 |
| Melting Onset (Solidus), °C | 1020 | |
| 1050 |
| Specific Heat Capacity, J/kg-K | 240 | |
| 390 |
| Thermal Expansion, µm/m-K | 14 | |
| 20 |
Electrical Properties
| Electrical Conductivity: Equal Volume, % IACS | 4.9 to 5.5 | |
| 17 |
| Electrical Conductivity: Equal Weight (Specific), % IACS | 3.5 to 3.9 | |
| 19 |
Otherwise Unclassified Properties
| Density, g/cm3 | 13 | |
| 8.2 |
Common Calculations
| Resilience: Ultimate (Unit Rupture Work), MJ/m3 | 13 to 100 | |
| 13 to 150 |
| Resilience: Unit (Modulus of Resilience), kJ/m3 | 1790 to 4660 | |
| 49 to 1900 |
| Stiffness to Weight: Axial, points | 4.7 | |
| 7.3 |
| Stiffness to Weight: Bending, points | 12 | |
| 19 |
| Strength to Weight: Axial, points | 18 to 27 | |
| 11 to 23 |
| Strength to Weight: Bending, points | 15 to 20 | |
| 13 to 21 |
| Thermal Shock Resistance, points | 41 to 61 | |
| 11 to 23 |
Alloy Composition
Deprecated: Automatic conversion of false to array is deprecated in /home/public/compare.php on line 452
| Copper (Cu), % | 13.5 to 14.5 | |
| 68.5 to 71.5 |
| Gold (Au), % | 9.5 to 10.5 | |
| 0 |
| Iron (Fe), % | 0 | |
| 0 to 0.1 |
| Lead (Pb), % | 0 | |
| 0 to 0.070 |
| Manganese (Mn), % | 0 | |
| 0.8 to 1.5 |
| Palladium (Pd), % | 34 to 36 | |
| 0 |
| Platinum (Pt), % | 9.5 to 10.5 | |
| 0 |
| Silver (Ag), % | 29 to 31 | |
| 0 |
| Zinc (Zn), % | 0.8 to 1.2 | |
| 26.3 to 30.7 |
| Residuals, % | 0 to 0.3 | |
| 0 to 0.5 |