ASTM B541 Gold vs. AWS BVAu-2
Both ASTM B541 gold and AWS BVAu-2 are otherwise unclassified metals. They have 86% of their average alloy composition in common. There are 15 material properties with values for both materials. Properties with values for just one material (9, in this case) are not shown.
For each property being compared, the top bar is ASTM B541 gold and the bottom bar is AWS BVAu-2.
Metric UnitsUS Customary Units
Mechanical Properties
| Elastic (Young's, Tensile) Modulus, GPa | 110 | |
| 100 |
| Poisson's Ratio | 0.4 | |
| 0.4 |
| Shear Modulus, GPa | 38 | |
| 36 |
| Tensile Strength: Ultimate (UTS), MPa | 670 to 1180 | |
| 150 |
Thermal Properties
| Latent Heat of Fusion, J/g | 90 | |
| 92 |
| Melting Completion (Liquidus), °C | 1110 | |
| 890 |
| Melting Onset (Solidus), °C | 930 | |
| 890 |
| Specific Heat Capacity, J/kg-K | 170 | |
| 180 |
| Thermal Expansion, µm/m-K | 13 | |
| 15 |
Otherwise Unclassified Properties
| Density, g/cm3 | 17 | |
| 17 |
Common Calculations
| Stiffness to Weight: Axial, points | 3.4 | |
| 3.3 |
| Stiffness to Weight: Bending, points | 9.0 | |
| 9.1 |
| Strength to Weight: Axial, points | 11 to 19 | |
| 2.4 |
| Strength to Weight: Bending, points | 9.8 to 14 | |
| 3.6 |
| Thermal Shock Resistance, points | 36 to 63 | |
| 7.1 |
Alloy Composition
Deprecated: Automatic conversion of false to array is deprecated in /home/public/compare.php on line 452
| Cadmium (Cd), % | 0 | |
| 0 to 0.0010 |
| Carbon (C), % | 0 | |
| 0 to 0.0050 |
| Copper (Cu), % | 13.5 to 15.5 | |
| 19.5 to 20.5 |
| Gold (Au), % | 70.5 to 72.5 | |
| 79.5 to 80.5 |
| Lead (Pb), % | 0 | |
| 0 to 0.0020 |
| Phosphorus (P), % | 0 | |
| 0 to 0.0020 |
| Platinum (Pt), % | 8.0 to 9.0 | |
| 0 |
| Silver (Ag), % | 4.0 to 5.0 | |
| 0 |
| Zinc (Zn), % | 0.7 to 1.3 | |
| 0 to 0.0010 |
| Residuals, % | 0 to 0.4 | |
| 0 |