ASTM B541 Gold vs. C22600 Bronze
ASTM B541 gold belongs to the otherwise unclassified metals classification, while C22600 bronze belongs to the copper alloys. There are 22 material properties with values for both materials. Properties with values for just one material (10, in this case) are not shown.
For each property being compared, the top bar is ASTM B541 gold and the bottom bar is C22600 bronze.
Metric UnitsUS Customary Units
Mechanical Properties
| Elastic (Young's, Tensile) Modulus, GPa | 110 | |
| 110 |
| Elongation at Break, % | 6.0 to 14 | |
| 2.5 to 33 |
| Poisson's Ratio | 0.4 | |
| 0.33 |
| Shear Modulus, GPa | 38 | |
| 42 |
| Shear Strength, MPa | 410 to 690 | |
| 220 to 320 |
| Tensile Strength: Ultimate (UTS), MPa | 670 to 1180 | |
| 330 to 570 |
| Tensile Strength: Yield (Proof), MPa | 480 to 900 | |
| 270 to 490 |
Thermal Properties
| Latent Heat of Fusion, J/g | 90 | |
| 200 |
| Melting Completion (Liquidus), °C | 1110 | |
| 1040 |
| Melting Onset (Solidus), °C | 930 | |
| 1000 |
| Specific Heat Capacity, J/kg-K | 170 | |
| 390 |
| Thermal Expansion, µm/m-K | 13 | |
| 18 |
Electrical Properties
| Electrical Conductivity: Equal Volume, % IACS | 7.7 to 12 | |
| 40 |
| Electrical Conductivity: Equal Weight (Specific), % IACS | 4.0 to 6.2 | |
| 42 |
Otherwise Unclassified Properties
| Density, g/cm3 | 17 | |
| 8.7 |
Common Calculations
| Resilience: Ultimate (Unit Rupture Work), MJ/m3 | 65 to 91 | |
| 14 to 100 |
| Resilience: Unit (Modulus of Resilience), kJ/m3 | 1090 to 3830 | |
| 330 to 1070 |
| Stiffness to Weight: Axial, points | 3.4 | |
| 7.2 |
| Stiffness to Weight: Bending, points | 9.0 | |
| 19 |
| Strength to Weight: Axial, points | 11 to 19 | |
| 11 to 18 |
| Strength to Weight: Bending, points | 9.8 to 14 | |
| 12 to 18 |
| Thermal Shock Resistance, points | 36 to 63 | |
| 11 to 19 |
Alloy Composition
Deprecated: Automatic conversion of false to array is deprecated in /home/public/compare.php on line 452
| Copper (Cu), % | 13.5 to 15.5 | |
| 86 to 89 |
| Gold (Au), % | 70.5 to 72.5 | |
| 0 |
| Iron (Fe), % | 0 | |
| 0 to 0.050 |
| Lead (Pb), % | 0 | |
| 0 to 0.050 |
| Platinum (Pt), % | 8.0 to 9.0 | |
| 0 |
| Silver (Ag), % | 4.0 to 5.0 | |
| 0 |
| Zinc (Zn), % | 0.7 to 1.3 | |
| 10.7 to 14 |
| Residuals, % | 0 to 0.4 | |
| 0 to 0.2 |