ASTM B563 Pd-Ag-Cu vs. Grade 5 Titanium
ASTM B563 Pd-Ag-Cu belongs to the otherwise unclassified metals classification, while grade 5 titanium belongs to the titanium alloys. There are 19 material properties with values for both materials. Properties with values for just one material (14, in this case) are not shown. Please note that the two materials have significantly dissimilar densities. This means that additional care is required when interpreting the data, because some material properties are based on units of mass, while others are based on units of area or volume.
For each property being compared, the top bar is ASTM B563 Pd-Ag-Cu and the bottom bar is grade 5 titanium.
Metric UnitsUS Customary Units
Mechanical Properties
| Elastic (Young's, Tensile) Modulus, GPa | 100 | |
| 110 |
| Elongation at Break, % | 7.0 to 17 | |
| 8.6 to 11 |
| Poisson's Ratio | 0.37 | |
| 0.32 |
| Shear Modulus, GPa | 37 | |
| 40 |
| Shear Strength, MPa | 470 to 690 | |
| 600 to 710 |
| Tensile Strength: Ultimate (UTS), MPa | 760 to 1170 | |
| 1000 to 1190 |
Thermal Properties
| Latent Heat of Fusion, J/g | 150 | |
| 410 |
| Melting Completion (Liquidus), °C | 1180 | |
| 1610 |
| Melting Onset (Solidus), °C | 1030 | |
| 1650 |
| Specific Heat Capacity, J/kg-K | 260 | |
| 560 |
| Thermal Expansion, µm/m-K | 14 | |
| 8.9 |
Electrical Properties
| Electrical Conductivity: Equal Volume, % IACS | 5.6 to 6.7 | |
| 1.0 |
| Electrical Conductivity: Equal Weight (Specific), % IACS | 4.6 to 5.5 | |
| 2.0 |
Otherwise Unclassified Properties
| Density, g/cm3 | 11 | |
| 4.4 |
Common Calculations
| Stiffness to Weight: Axial, points | 5.2 | |
| 13 |
| Stiffness to Weight: Bending, points | 14 | |
| 35 |
| Strength to Weight: Axial, points | 19 to 30 | |
| 62 to 75 |
| Strength to Weight: Bending, points | 17 to 22 | |
| 50 to 56 |
| Thermal Shock Resistance, points | 39 to 61 | |
| 76 to 91 |
Alloy Composition
Deprecated: Automatic conversion of false to array is deprecated in /home/public/compare.php on line 452
| Aluminum (Al), % | 0 | |
| 5.5 to 6.8 |
| Carbon (C), % | 0 | |
| 0 to 0.080 |
| Copper (Cu), % | 15.5 to 16.5 | |
| 0 |
| Hydrogen (H), % | 0 | |
| 0 to 0.015 |
| Iron (Fe), % | 0 | |
| 0 to 0.4 |
| Nickel (Ni), % | 0.8 to 1.2 | |
| 0 |
| Nitrogen (N), % | 0 | |
| 0 to 0.050 |
| Oxygen (O), % | 0 | |
| 0 to 0.2 |
| Palladium (Pd), % | 43 to 45 | |
| 0 |
| Platinum (Pt), % | 0.8 to 1.2 | |
| 0 |
| Silver (Ag), % | 37 to 39 | |
| 0 |
| Titanium (Ti), % | 0 | |
| 87.4 to 91 |
| Vanadium (V), % | 0 | |
| 3.5 to 4.5 |
| Yttrium (Y), % | 0 | |
| 0 to 0.0050 |
| Residuals, % | 0 to 0.4 | |
| 0 to 0.4 |