MakeItFrom.com
Menu (ESC)

ASTM B563 Pd-Ag-Cu vs. Solder Alloy 151

Both ASTM B563 Pd-Ag-Cu and solder alloy 151 are otherwise unclassified metals. There are 18 material properties with values for both materials. Properties with values for just one material (7, in this case) are not shown.

For each property being compared, the top bar is ASTM B563 Pd-Ag-Cu and the bottom bar is solder alloy 151.

Metric UnitsUS Customary Units

Mechanical Properties

Elastic (Young's, Tensile) Modulus, GPa 100
39
Elongation at Break, % 7.0 to 17
37
Poisson's Ratio 0.37
0.37
Shear Modulus, GPa 37
14
Tensile Strength: Ultimate (UTS), MPa 760 to 1170
46

Thermal Properties

Latent Heat of Fusion, J/g 150
47
Melting Completion (Liquidus), °C 1180
150
Melting Onset (Solidus), °C 1030
150
Specific Heat Capacity, J/kg-K 260
190
Thermal Expansion, µm/m-K 14
26

Electrical Properties

Electrical Conductivity: Equal Volume, % IACS 5.6 to 6.7
10
Electrical Conductivity: Equal Weight (Specific), % IACS 4.6 to 5.5
10

Otherwise Unclassified Properties

Density, g/cm3 11
8.8

Common Calculations

Stiffness to Weight: Axial, points 5.2
2.5
Stiffness to Weight: Bending, points 14
13
Strength to Weight: Axial, points 19 to 30
1.4
Strength to Weight: Bending, points 17 to 22
3.2
Thermal Shock Resistance, points 39 to 61
3.2

Alloy Composition


Deprecated: Automatic conversion of false to array is deprecated in /home/public/compare.php on line 452
Aluminum (Al), % 0
0 to 0.0010
Antimony (Sb), % 0
0 to 0.2
Arsenic (As), % 0
0 to 0.030
Bismuth (Bi), % 0
0 to 0.1
Cadmium (Cd), % 0
17.5 to 18.5
Copper (Cu), % 15.5 to 16.5
0 to 0.080
Gold (Au), % 0
0 to 0.050
Indium (In), % 0
0 to 0.1
Iron (Fe), % 0
0 to 0.020
Lead (Pb), % 0
30.3 to 33
Nickel (Ni), % 0.8 to 1.2
0 to 0.010
Palladium (Pd), % 43 to 45
0
Platinum (Pt), % 0.8 to 1.2
0
Silver (Ag), % 37 to 39
0 to 0.1
Tin (Sn), % 0
49.5 to 50.5
Zinc (Zn), % 0
0 to 0.0010
Residuals, % 0 to 0.4
0