ASTM B596 Au-Cu vs. ASTM B477 Au-Ni-Ag
Both ASTM B596 Au-Cu and ASTM B477 Au-Ni-Ag are otherwise unclassified metals. They have 75% of their average alloy composition in common. There are 19 material properties with values for both materials. Properties with values for just one material (1, in this case) are not shown.
For each property being compared, the top bar is ASTM B596 Au-Cu and the bottom bar is ASTM B477 Au-Ni-Ag.
Metric UnitsUS Customary Units
Mechanical Properties
| Elastic (Young's, Tensile) Modulus, GPa | 100 | |
| 95 |
| Elongation at Break, % | 4.3 to 17 | |
| 5.5 to 11 |
| Poisson's Ratio | 0.41 | |
| 0.41 |
| Shear Modulus, GPa | 36 | |
| 34 |
| Shear Strength, MPa | 280 to 360 | |
| 190 to 320 |
| Tensile Strength: Ultimate (UTS), MPa | 450 to 620 | |
| 310 to 550 |
Thermal Properties
| Latent Heat of Fusion, J/g | 77 | |
| 80 |
| Melting Completion (Liquidus), °C | 1060 | |
| 1010 |
| Melting Onset (Solidus), °C | 930 | |
| 930 |
| Specific Heat Capacity, J/kg-K | 150 | |
| 160 |
| Thermal Expansion, µm/m-K | 14 | |
| 15 |
Electrical Properties
| Electrical Conductivity: Equal Volume, % IACS | 14 | |
| 14 |
| Electrical Conductivity: Equal Weight (Specific), % IACS | 6.7 | |
| 7.5 |
Otherwise Unclassified Properties
| Density, g/cm3 | 18 | |
| 17 |
Common Calculations
| Stiffness to Weight: Axial, points | 3.1 | |
| 3.1 |
| Stiffness to Weight: Bending, points | 8.5 | |
| 8.9 |
| Strength to Weight: Axial, points | 6.8 to 9.4 | |
| 5.0 to 9.0 |
| Strength to Weight: Bending, points | 7.1 to 8.8 | |
| 6.0 to 8.8 |
| Thermal Shock Resistance, points | 22 to 30 | |
| 16 to 28 |
Alloy Composition
Deprecated: Automatic conversion of false to array is deprecated in /home/public/compare.php on line 452
| Copper (Cu), % | 9.0 to 11 | |
| 0 |
| Gold (Au), % | 89 to 91 | |
| 74.2 to 75.8 |
| Nickel (Ni), % | 0 | |
| 2.6 to 3.4 |
| Silver (Ag), % | 0 | |
| 21.4 to 22.6 |
| Residuals, % | 0 to 0.4 | |
| 0 to 0.3 |